Equilibrium Distribution Ratio of Phosphorus between Solid Iron and Magnesiowustite-saturated Al2O3–CaO–FetO–MgO–SiO2 Slag at 1623 K
スポンサーリンク
概要
- 論文の詳細を見る
In the conventional iron-making process, the oxygen potential in the hearth of the blast furnace is determined only by the temperature because of the carbon-saturated conditions. As a consequence, impurities such as phosphorus are reduced and dissolved in the iron because of the excessively low oxygen partial pressure. The oxygen partial pressure can be controlled by using gas reductants such as hydrogen and carbon monoxide. Under these conditions, solid iron is obtained because of the low carbon content. In this study, the equilibrium distribution of phosphorus between the solid iron and molten slag is investigated at 1623 K as functions of the oxygen partial pressure and the basicity of the slag. The experimental results show that the phosphorus content in the solid iron is sufficiently low under the experimental conditions employed. The phosphate capacity is also evaluated, and a regression equation is obtained by comparing the results with those of previous studies.
- The Iron and Steel Institute of Japanの論文
著者
-
Maruoka Nobuhiro
Institute Of Multidisciplinary Research For Advanced Materials Tohoku University
-
Kitamura Shin-ya
Institute Of Multi-disciplinary Research On Advanced Materials Tohoku University
-
Shibata Hiroyuki
Institute For Advanced Materials Processing Tohoku University
-
Ono Shinpei
Formerly Graduate School of Engineering, Tohoku University
関連論文
- High Thermal Conductivity of Gallium Nitride (GaN) Crystals Grown by HVPE Process
- Electrical Resistivity Measurements of Pd_Cu_Ni_P_ Alloy in Supercooled Liquid and Liquid State
- Thermal Diffusivities and Conductivities of Molten Germanium and Silicon
- Measurement of Thermal Diffusivity of Steels at Elevated Temperature by a Laser Flash Method
- Applicability of Platinum and Molybdenum Coatings for Measuring Thermal Diffusivity of Transparent Glass Specimens by the Laser Flash Method at High Temperatures
- In-situ Observation of Intragranular Ferrite Nucleation at Oxide Particles
- Molecular Properties and Activity of Amino-Terminal Truncated Forms of Lipase Activator Protein
- Calcium Ion-Dependent Reactivation of a Pseudomonas Lipase by Its Specific Modulating Protein, LipB^1
- Analysis on Material and Energy Balances of Ironmaking Systems on Blast Furnace Operations with Metallic Charging, Top Gas Recycling and Natural Gas Injection
- Analysis of Dephosphorization Reaction Using a Simulation Model of Hot Metal Dephosphorization by Multiphase Slag
- Modeling the Behavior of Al_2O_3 Inclusions during the Dendritic Solidification of Steel
- Effect of Bottom Bubbling Conditions on Surface Reaction Rate in Oxygen-Water System
- Behavior of Cobalt in Iron- and Steel-making Processes
- Distribution of P_2O_5 between Solid Dicalcium Silicate and Liquid Phases in CaO-SiO_2-Fe_2O_3 System
- Prediction of Raceway Shape and Size
- Mass Transfer of P_2O_5 between Liquid Slag and Solid Solution of 2CaO・SiO_2 and 3CaO・P_2O_5
- Origin of Heat Transfer Anomaly and Solidifying Shell Deformation of Peritectic Steels in Continuous Casting
- Recovery of Hot Ductility by Improving Thermal Pattern of Continuously Cast Low Carbon and Ultra Low Carbon Steel Slabs for Hot Direct Rolling
- Distribution of P_2O_5 between Solid Solution of 2CaO・SiO_2-3CaO・P_2O_5 and Liquid Phase
- Precipitation Behavior of Copper, Tin and Manganese Sulfide at High Temperature in Fe-10%Cu-0.5%Sn Alloys
- Determination of Free Energy of δ-Ferrite/γ-Austenite Interphase Boundary of Low Carbon Steels by In-situ Observation
- In-situ Observation of Engulfment and Pushing of Nonmetallic Inclusions in Steel Melt by Advancing Melt/Solid Interface
- Characteristics of Agglomeration of Various Inclusion Particles on Molten Steel Surface
- "In-situ"Observation of Collision, Agglomeration and Cluster Formation of Alumina Inclusion Particles on Steel Melts
- Heat Transfer across Mold Flux Film in Mold during Initial Solidification in Continuous Casting of Steel
- Thermal Resistance at the Interface between Mold Flux Film and Mold for Continuous Casting of Steels
- Radiative Heat Transfer through Mold Flux Film during Initial Solidification in Continuous Casting of Steel
- Heat Transfer from Shell across Flux Film to Continuous Casting Mold
- Measurement of Optical Properties of Continuous Casting Mold Fluxes at Elevated Temperatures
- Thermal Resistance between Solidifying Steel Shell and Continuous Casting Mold with Intervening Flux Film
- Anomaly in Melting Behavior and Mechanical Properties of Carbon Steels Near Their Solidus Temperature
- "In-situ"Real Time Observation of Planar to Cellular and Cellular to Dendritic Transition of Crystals Growing in Fe-C Alloy Melts
- Chemical State of Chromium in CaO-SiO_2 Base Oxides Annealed under Different Conditions
- Distribution of Cobalt between MgO-Saturated FeO_x-MgO-CaO-SiO_2 Slag and Fe-Cu-Co Molten Alloy
- On the Nuclear Interaction of Mu-Mesons
- Development of PCM Reactor for Methane Steam Reforming
- Exergy Analysis of Methane Steam Reformer Utilizing Steelmaking Waste Heat
- Influence of Bottom Bubbling Condition on Metal Emulsion Formation in Lead-Salt System
- Degree of Undercooling and Contact Angle of Pure Iron at 1933K on Single-crystal Al_2O_3, MgO, and MgAl_2O_4 under Argon Atmosphere with Controlled Oxygen Partial Pressure
- Evaluation of Bubble Eye Area to Improve Gas/Liquid Reaction Rates at Bath Surfaces
- Estimation of Heat Transfer of a Front-heating Front-detection Laser Flash Method Measuring Thermal Conductivity for Silicate Melts at High Temperatures
- Thermal and Optical Properties of Yb3+-Doped Y2O3 Single Crystal Grown by the Micro-Pulling-Down Method
- Behavior of Vanadium and Niobium during Hot Metal Dephosphorization by CaO-SiO_2-Fe_tO Slag
- Influence of Solid CaO and Liquid Slag on Hot Metal Desulfurization
- Mechanism of Change in Chemical Composition of Oxide Inclusions in Fe-Cr Alloys Deoxidized with Mn and Si by Heat Treatment at 1473 K
- Preface to the Special Issue on "Fundamentals and Applications of Non-metallic Inclusions in Solid Steel"
- Influence of Bottom Bubbling Rate on Formation of Metal Emulsion in Al–Cu Alloy and Molten Salt System
- Influence of Bottom Bubbling Rate on Formation of Metal Emulsion in Al-Cu Alloy and Molten Salt System
- Influence of Slag Basicity and Temperature on Fe and Mn Distribution between Liquid Fe–Mn–Ca–O–S Matte and Molten Slag
- Equilibrium Distribution Ratio of Phosphorus between Solid Iron and Magnesiowustite-saturated Al2O3–CaO–FetO–MgO–SiO2 Slag at 1623 K