ウィスカライジングによる炭素繊維 / 炭素複合体強度改善の試み

スポンサーリンク

概要

• 論文の詳細を見る

• Carbon/Carbon (C/C) composites are of importance in the field of aerospace engineering. Two methods have so far been proposed for the production of the C/C composites: impregnation of carbon fiber (CF) fillers with pitch or resin followed by carbonization, and infiltration of the fillers with pyrolytic carbon. But, linkage between the fillers and the matrices is not satisfactory. To improve the linkage, in the present work the effect of whiskerization of the fillers with carbon micro fibers has been examined. Ptch-based commercial CF paper was used as a filler. Carbon microfibers of 0.1 -0.5 μm diameter and 20-60 μm length were grown on the CF paper by thermal decomposition of benzene at 1100℃ in the presence of iron and hydrogen sulfide as catalysts. The resulting whiskerized CF paper was then infiltrated with pyrolytic carbon (PC) under various conditions. Benzene diluted with nitrogen was also used as the source materials of PC. Infiltration with PC was most effective under the conditions of CsHs concentration 4-5%, reactant flow rate 450-600cm3/min, and pyrolysis temperature 1100℃. However, it was extremely difficult to fill up the inner space of the CF paper with PC. Thus, many voids were left behind even under the optimum conditions. The three point bending strength of the whiskerized CF paper was only 0.2-0.4 kg/mm2, which was lower than that of the as-recieved CF paper because of deterioration of the CF paper itself. On the other hand, the bending strength of the C/C composite based on the whiskerized CF paper increased to 2-3 kg/mm2, but it was approximately the same as that for the composite based on the non-whiskerized CF paper. Only a slight increase in the Young's modulus was attained by the whiskerization treatment.

• 長崎大学工学部,Faculty of Engineering, Nagasaki Universityの論文

著者

• 勝木 宏昭

  Department of Materials Science and Engineering, Faculty of Engineering, Nagasaki University

• 勝木 宏昭

  Department Of Materials Science And Engineering Faculty Of Engineering Nagasaki University

関連論文

• 転写印刷法により作製した WO_3 系半導体ガスセンサの NO_X 検知特性
• 28a-J-9 SnO_2ウィスカーのモルフォロジー
• 六方晶BN中の転位
• β-SiCウイスカー中の積層欠陥(セラミックスの微細構造)
• β-SiC whisker中の積層欠陥
• 半導体ガスセンサ基板の多孔質化
• 硫化ケイ素と水蒸気の反応によるSiO_2微粒子の合成
• 硫黄含有シリコーンオイルの熱分解によるβ-SiCウイスカーの生成と機械的性質
• ウィスカライジングによる炭素繊維 / 炭素複合体強度改善の試み
• 単斜晶ZrO_2ウイスカーの気相成長(2. 気相反応法)(新技術によるセラミックスの合成と評価(I))
• 炭素繊維のTiCコーティング
• 硫化ケイ素を中間体とするβ-SiCウイスカーの気相成長
• 炭素の気相成長における鉄触媒の粒径効果
• 炭素繊維を密生させた炭素材の製造-3-ポリアクリロニトリル系およびピッチ系炭素繊維上でのカ-ボンウィスカ-の生成
• 炭素体の気相からの成長における触媒の働き (触媒のいろいろな応用)
• ベンゼンからの炭素繊維の気相成長における各種金属および炭素基板の効果
• 酸化亜鉛の表面構造とプロピレン酸化活性

もっと見る 閉じる

スポンサーリンク