部分溶融法によるイットリウム系超伝導体の作成Ⅱ

スポンサーリンク

概要

• 論文の詳細を見る

• YBa2Cu3Oy superconductors have been fabricated by a combination process of solid state reaction and partial melting. Sintering the YBa2Cu3Oy results in extremely small grains, which in turn produce uniformly distributed fine Y2BaCuO5 grains during partial melting. Y2BaCuO5 acts as the nucleation site for peritectic reaction. The unreacted Y2BaCuO5 seems to act as a flux pinning center. In last year study, that seemed a pinning center was, in fact, unreacted part of YBa2Cu3Oy(1100℃,10min). In this year, authors have made a superconductor in which the time and temperature of melting is changed. Due to this flux pinning force, YBa2Cu3Oy superconductors having the melting temperature from l075℃ to 1100℃ and melting time of 30min have a little unreacted part.

• 津山工業高等専門学校の論文
• 1994-11-21

著者

• 原田 寛治

  電気電子工学科

関連論文

• Fabrication of All-High-Tc Josephson Junction by Plasma Treatment
• 三層構造超伝導バルクの作製
• イットリウム系酸化物超伝導薄膜に関する研究
• 津山高専志願者の確保のための電気電子工学科の試み
• 超伝導薄膜における液相の拡散
• 部分溶融法による液相の拡散
• バルク超伝導体の保護膜による磁気浮上特性
• 新しいコンピュータ環境に適する教育課題の研究
• 部分溶融法によるイットリウム系超伝導体の作成Ⅱ
• 部分溶融法によるイットリウム系超伝導体の作成
• イットリウム系超伝導薄膜のバイアス電圧効果
• 酸化物超伝導体に関する研究Ⅱ
• 酸化物超伝導に関する研究

もっと見る 閉じる

スポンサーリンク