Melt-processed YBa2Cu3Oy,(Y123) superconductors are highly attractive for bulk applications, such as strong superconducting bulk magnets. Phase diagram shows a peritectic point at about 1010℃ where Y2BaCuO5(Y211), a liquid and Y123 coexist. We have investigated the diffusion in both the Y123 and Y211 systems using the partial melting. We put the Y123 superconducting bulk between the Y211 bulks. The conditlons of partial melting were 1040℃-5 minutes. As the result, we could have the Y211 film in the Y123 superconducting bulk named two layer structures. Furthermore we put the two layer structures between Y123 bulks and condition of repartial melting were 1040℃-5minutes. This process is possible to produce tri-layer structures. It was shown that levitating force in this superconducting bulk by meissner effect had a higher than one in the Y123 superconductor without Y211 film at 77K.
- 津山工業高等専門学校の論文
- 2003-01-31
著者
関連論文
- Fabrication of All-High-Tc Josephson Junction by Plasma Treatment
- 三層構造超伝導バルクの作製
- イットリウム系酸化物超伝導薄膜に関する研究
- 津山高専志願者の確保のための電気電子工学科の試み
- 超伝導薄膜における液相の拡散
- 部分溶融法による液相の拡散
- バルク超伝導体の保護膜による磁気浮上特性
- 新しいコンピュータ環境に適する教育課題の研究
- 部分溶融法によるイットリウム系超伝導体の作成Ⅱ
- 部分溶融法によるイットリウム系超伝導体の作成
- イットリウム系超伝導薄膜のバイアス電圧効果
- 酸化物超伝導体に関する研究Ⅱ
- 酸化物超伝導に関する研究