極低温小形パンチ試験によるオーステナイト系ステンレス鋼JN1,JJ1およびJK2の熱時効脆化評価

概要

論文の詳細を見る
The small punch (SP) tests were conducted at 77 K and 4 K using austenitic stainless steels JN 1, JJ 1 and JK 2, which have been recently developed for use as a cryogenic structural material. The tests were applied to the steels aged at 923-1073K to investigate changes in their toughness at cryogenic temperature due to thermal aging. The area under the load-deflection curve up to the macro-crack initiation was defined as SP energy to evaluate the fracture toughness of the steels. The experimental results showed that the SP energy of JN 1 decreased monotonously with an increase in aging temperature. On the other hand, the SP energy of JK 2 showed no significant change even after the thermal aging at 923 K and 973 K and decreased after the thermal aging at 1023 K. Metallographic examination revealed that this difference in decrease of SP energy due to thermal aging was caused by the variation in amount and distribution of grain boundary M_<23>C_6 carbides. As a consequence, JN 1 was more susceptible to thermal aging embrittlement than the other steels, and high resistance of JK 2 to embrittlement was attributable to the depression of precipitation and coarsening of grain boundary precipitates.
社団法人日本機械学会の論文
2004-04-25