高速重ねシーム溶接の接合部形成現象の基礎的研究(第 1 報) : 接合部形成に及ぼす主溶接条件の影響

概要

論文の詳細を見る
The influences of welding current, welding speed and electrode force on the size and shape of the nugget and HAZ, indentation and weld formation process are studied using cold rolled mild steel having thickness of 1.2mm. The results obtained are as follows. Nugget width, penetration and indentation increase with the increase of welding current and the upper limit of welding current is restricted by the occurance of surface flash. As welding speed increases the rate of increase of penetration as against the increase of current becomes larger which restricts the upper limit of welding speed. Increased electrode force enlarges the weldable welding current range, especially under high speed condition. According to the observation of longitudinal sections, weld formation process can be divided into two types with welding speed. In case of an electrode force of 480kg, the transition welding speed is about 4m/min which coincides with the welding speed at which melting efficiency is saturated.
社団法人溶接学会の論文
1977-08-05