熱影響部の脆化について(第 2 報) : Single Bead による脆化
スポンサーリンク
概要
- 論文の詳細を見る
In this experiment the authors investigated the true reasons causing the brittleness in the range of heat-affected zone by observing Izod impact test, hardness measurement and Xray diffraction method in the single bead weld, and compared the states of the brittleness about both Killed and Rimmed steel. As the result it was recognized that the main factor to cause brittleness is the precipitation of super-saturated carbon in ferrite grain, and that state is used to caused by the rapid cooling from the neighbour of A_1 transformation point, and the most brittle part of Killed steel seems to somewhat above A_1,Rimmed steel somewhat below A_1,i.e. the mechanisms causing brittleness are somewhat different. The brittleness of Rimmed steel is more predominent than Killed steel.
- 社団法人溶接学会の論文
著者
関連論文
- (11) イルメナイト型溶接棒の耐亀裂性とスラグの塩基度(昭和 37 年度春季学術講演会講演概要)
- 放射性同位元素 S^ による研究(第 2 報) : 母材 S の熔着金属えの拡散について
- 放射性同位元素 S^ による研究(第 1 報)
- 熱影響部の脆化について(第 8 報) : 予歪と脆化領域
- 耐摩耗性肉盛溶接用合金について
- 熱影響部の脆化について(第 5 報) : 補遺綜合衝撃試驗片の幅の効果
- 軟鋼熔着金属中の Mo と低温脆性
- 熱影響部の脆化について(第 4 報) : 低温脆性について
- 熱影響部の脆化について(第 3 報) : 低水素型及びイルミナイト型の衝撃値分布
- 熱影響部の脆化について(第 2 報) : Single Bead による脆化
- 熱影響部の脆化について(第 1 報) : キルド鋼, リムド鋼の熱処理効果
- 第 5 班(熔接關係)(第 1 回世界冶金會議)
- 熔着金屬の Gas-Inclusion について(第 1 報) : 熔着金属の Gas-Inclusion と機械的性質との関係
- 米國に於ける潜弧熔接用熔剤, 線材を調査して
- イルミナイト系熔接棒の主要熔剤の粒度の影響
- (18) ユニオンメルトフラツクスの物理性質について(第 1 報.第 2 報)
- (17) ユニオンメルト熔接における諸現象について
- (16) ユニオンメルトにおけるリンデ型とリンカーン型との比較
- (8) 低水素型熔接棒について
- (6) 被覆剤中の硫黄の擧動について
- (5) 被覆剤中の燐の擧動について
- (3) 熔着金属の機械的性質におよぼす諸元素の影響の推計的考察
- 最近の熔接棒について
- 熱影響部の脆化について(第 7 報) : 綜合衝撃法による低温脆性の研究
- 熱影響部の脆化について(第 5 報) : 綜合衝撃試驗法について
- 1 溶接部のミクロ的な不均一性と継手の強度
- Cuの凍結空孔 : 格子欠陥
- 4a-E-1 溶着鋼中の酸化介在物に関するX線的研究
- 多層熔接部の脆化, 熱処理による回復(その 2)
- 熱影響部の脆化について(第 6 報) : 多層熔接部の脆化, 熱処理による回復(その 1)
- deep fillet 熔接棒 (II)
- Deep Fillet 熔接棒 (I)
- 曲げ試験について
- 熔接部の窒素に関する物理的研究(第 1 報)
- 軟鋼熔接部の活性化エネルギーについて(第 2 報)
- 軟鋼熔接部の活性化エネルギーについて (I)
- 8. 軟鋼熔接部の活性化エネルギーについて