On-line size exclusion chromatography/nuclear magnetic resonance (SEC/NMR) has been applied to the characterization of polymers. In this study, on-line SEC/NMR was applied to an analysis of silicone, and a suitable condition for determining the molecular weight dependence of the functional groups in silicone was investigated. Deuterated chloroform was used as an eluent, the flow rate was 0.04 ml/min. The amount of sample was 10 mg. A presaturation method was used to reduce the highest signal due to SiCH_3. The ^1H-NMR spectra were collected every 225 s. Each spectrum was obtained by the accumulation of 420 scans. By on-line SEC/NMR using the above-mentioned condition, a distribution analysis of 10^<-5> eq./g order of functional groups in silicone has become feasible. It was also found that the times required for a sample treatment and an analysis were 1/30 and 1/3 of the off-line time, respectively. Applications to the analysis of adhesives have proved that this method is useful for the analysis of silicone.
- 社団法人日本分析化学会の論文
- 2001-03-05
著者
関連論文
- 誘導体化を併用するX線マイクロアナリシスによる高分子材料中の官能基の分布分析
- 銀蒸着/飛行時間型二次イオン質量分析法による固体表面でのシリコーンオイルの分子量評価
- 誘導体化-電子線プローブマイクロアナリシス法による高分子中の微量官能基の分布公析
- 誘導体化/電子プローブX線マイクロアナリシスによる高分子材料中のカルボニル基の分布分析
- 誘導体化-EPMA法による高分子材料中の微量官能基の分布分析
- 誘導体化/電子線プローブマイクロアナリシスによる高分子材料中のカルボキシル基の分布分析 : 誘導体化/EPMA法の開発(第2報)
- ポリウレタンフォームを裏打ちした軟質ポリ塩化ビニルの劣化メカニズムの解析
- 誘導体化-電子線プローブマイクロアナリシスによるポリ塩化ビニル中の微量官能基の分布分析
- 不飽和ポリエステル樹脂の架橋構造の解析
- 表面増強赤外分光法を利用した液体クロマトグラフィー/赤外分光法による高分子材料中の添加剤の分析
- サイズ排除クロマトグラフィー/核磁気共鳴法によるシリコーン中の官能基の分布分析
- 第5回高分子分析討論会
- 高分子材料の劣化評価法