炭素鋼の気液二相流中***ージョン・コロージョン損傷機構と損傷発生条件

概要

論文の詳細を見る
The erosion-corrosion characteristics of carbon steel commonly used as piping material subjected to an impinging gas-liquid two-phase flow under various pH. chloride ion concentration and flow rate combinations were investigated. Environmental condition saffected not only the damage rate but also the type of damage. One of these was the enhanced general corrosion observed mainly under high chlorine ion concentration (1220ppm) and another was flow-induced pitting corrosin observed under the pH7-[C1^-] 140ppm condition. Each condition of the chemical solution had its own flow effect. For example, in the case of high chlorine ion concentration, high flow rate accelerated corrosion damage by decreasing diffusion control. On the other hand, under low chlorine ion concentration, high-speed flow decreased the corrosion rate by the action of removing nonprotective oxide layer. To indicate the condition of occurrence for enhanced corrosion damage, a two-dimensional chart which had axes of [C1^-] concentration and flow rate was constructed for each pH value.
社団法人日本機械学会の論文
1989-11-25