経年劣化CrMoV鋳鋼平滑材における微小き裂の発生と成長挙動

概要

論文の詳細を見る
Micro-crack initiation and growth behavior were observed on the surface of nondegraded and degraded CrMoV cast steels under various strain wave shape loadings at a high temperature. The degraded steel was taken from the inside of a main steam valve casing after 140 000 h of service. No significant difference in crack growth behavior was observed in low cycle fatigue in both steels ; however, the crack growth rate in the degraded steel was higher than that in the nondegraded one in creep fatigue under S-F straining. This was caused mainly by coarsened grain boundary carbides. A residual life assessment method, based on micro-crack growth and the statistical properties of micro-crack length distribution, gives an estimation close to the experimental results.
一般社団法人日本機械学会の論文
1987-03-25