温度変動繰返し変形条件下における改良9Cr-1Mo鋼の非弾性構成式 : 第1報, 等温および温度変動繰返し変形下における非弾性変形挙動と内部状態変数

概要

論文の詳細を見る
A series of cyclic deformation tests was conducted on modified 9 Cr-1 Mo steel at various temperatures, including nonisothermal conditions to investigate inlastic behavior of the material. The material showed cyclic softening behavior under temperatures between 200℃ and 600℃, and its degree got larger as the temperature was increased. Temperature history effect was scarcely found except the case where the test temperature was changed from high to low after large cyclic softening at the high temperature. Peak stress under thermomechanical conditions showed approximately the same value as those observed under corresponding isothermal condition. Furthermore, internal state variables used in the authors' unified constitutive model were experimentally measured. An aging stress, which corresponds to resistance by dynamic strain aging effect, and an effective stress were almost constant under cyclic deformation conditions, while a back stress showed eminent cyclic softening behavior.
一般社団法人日本機械学会の論文
1999-04-25