2.25Cr-1Mo鋼ボイラ溶接熱影響部の高温強度特性評価

概要

論文の詳細を見る
ln view of the situation that aging of boiler components proceeds and some"Type IV"cracking incidents are reported recently, the develoment of an accurate remaining life evaluation method for boiler weldment parts is an important subject for the utilities. In this study, simulated materials with coarse and fine grain microstructures in a weldment heat affected zone were produced, and their high temperature strength properties were evaluated. The strength property of the weld joint was also discussed based on the experimental and analytical results. It was found that the creep rupture strength of the fine grain material was as low as 1/2 of the base metal and as 1/5 of the coarse grain material, and the weld joint ruptured at the fine grain region in a shorter period than the base metal as the applied stress level decreased. Many grainboundary creep cavities were also observed in the fine grain region. A creep deformation analysis by FEM indicated that the creep strain accumulation at the fine grain region in the weld joint preceded against other regions, suggesting that the rupture of weld joint occurred at the fine grain region in the experiment.
1998-03-15