Cu/Si_3N_4傾斜機能材料の静的強度評価

概要

論文の詳細を見る
In order to ensure reliability of the thermoelectric module, we had applied a FGM layer with composition of Cu and Si_3N_4 to the bonding parts in the module and decided the functionally graded compositional profile based on numerical analysis. In this study, Cu/Si_3N_4 functionally gradient material and Cu/Si_3N_4 composite materials were fabricated by hot press (HP) and static strength at room temperature was evaluated. As a result, it was found by observation with an optical microscope that neither FGM nor the composite materials produced by HP had internal defects. Static strength of composite materials obtained by the 4-point bending test exhibited a lower value as compared with those based on the rule of linear mixture. Finite element analysis for the FGM was performed. It was shown that fractured stress and initiation site of cracks could be predicted by using the fracture criterion for the bending strength of the composite materials.
一般社団法人日本機械学会の論文
1996-09-25