酸化物超伝導体の破壊強度・靱性評価と破壊過程での超伝導性
スポンサーリンク
概要
- 論文の詳細を見る
Tensile strength of sintered YBCO superconductor at 77K was evaluated by Brazilian test and fracture toughness at 85K was measured by use of round compact tention specimen. Superconductivity of specimens during Brazilian tests were examined by the four-point terminal method. Density of a specimen was the principal factor of tensile strength and the fracture surface exhibited the cleavage-intergranular mixed pattern. No change in superconductivity of specimens was observed until mechanical fracture occurred. Namely, no stress dependence on superconductivity was observed for these material tested. Fracture toughness K_Q of sintered YBCO was also measured by use of a round compact specimen. The K_Q value of sintered YBCO with a density of 4,84g/cm^3 was 1.1Mpa・m^<l/2>. The obtained K_Q shows the value of one third or quarter compared with that of ordinary ceramics (ZrO_2, Al_2O_3).
- 社団法人日本機械学会の論文
- 1989-04-25
著者
関連論文
- 酸化皮膜の特徴抽出に基づく炭素鋼FAC速度の考察(第14回動力・エネルギー技術シンポジウム)
- 低酸化性および還元性超臨界水環境におけるNi基およびFe基合金の腐食評価
- 1009 超臨界水環境における応力腐食割れ感受性評価
- 磁気光学素子を用いた新しい非破壊探傷
- 間欠暖房と割増率(構造・防災・環境工学・材料)
- 408 電気化学的過渡信号に着目したSCC・局部腐食発生過程の観測手法の開発(OS3-1 非破壊検査,OS3 エネルギー構造機器の健全性評価と信頼性の高度化3)
- 炭素鋼表面き裂材の腐食疲労き裂進展挙動に関する破壊力学的研究
- 水素ガス環境下での低合金鋼のき裂進展挙動とAE放出特性の評価
- A106 炭素鋼FAC速度に及ぼす材料組成ならびに水質因子の影響評価(配管減肉(FAC),OS6 保全・設備診断技術(1),一般講演,地球温暖化防止と動力エネルギー技術)
- A106 炭素鋼FAC速度に及ぼす材料組成ならびに水質因子の影響評価(配管減肉(FAC),OS6 保全・設備診断技術(1),一般講演,地球温暖化防止と動力エネルギー技術)