熱応力緩和層を有するZrO_2/Ni系遮熱コーティング材料のNTO/MMH燃焼ガス加熱場におけるレーザ改質効果
スポンサーリンク
概要
- 論文の詳細を見る
Evaluation test of the laser cracking specimens applied to the ZrO_2/Ni functionally graded materials (FGM) and also applied to the non-FGM has been described. In this test, 30 mm disk specimens of these materials were exposed to the combustion gas of nitrogen tetroxide (NTO)/monomethyl hidrazine (MMH) propellant. The delamination and the vertical crack formation of the ZrO_2 thermal barrier coating were observed during the heating test. It has been found that the laser cracking method seemed to be effective at preventing delamination in the coating layer of the test specimens. The crack and the delamination formation mechanism for ZrO_2/Ni FGM test specimens were also discussed with a thermal stress analysis by using a finite element method.
- 社団法人日本機械学会の論文
- 1998-05-25
著者
-
新野 正之
JAST
-
須藤 孝幸
宇宙開発事業団
-
庄子 哲雄
東北大学工学部附属破壊力学応用研究施設
-
森谷 信一
航空宇宙技術研究所
-
新野 正之
航空宇宙技術研究所
-
新野 正之
航技研
-
黒田 行郎
航空宇宙技術研究所
-
佐藤 政裕
宇宙航空研究開発機構 総合技術研究本部 宇宙推進技術共同センター
-
新野 正之
航空宇宙財団
-
新野 正之
科学技術庁航空宇宙技術研究所
-
新野 正之
航技研角田
-
毛呂 明夫
航空宇宙技術研究所
-
張 清杰
武漢理工大学
-
佐藤 政裕
航空宇宙技術研究所
-
新野 正之
航空宇宙技術研究所角田宇宙推進技術研究所
-
張 清杰
武漢工業大学
-
只野 真
宇宙航空研究開発機構 総合技術研究本部 宇宙推進技術共同センター
-
森谷 信一
航技研角田
-
只野 真
航空宇宙技術研究所
-
森谷 信一
航空宇宙技術研
-
新野 正之
航空宇宙技術振興財団
-
庄子 哲雄
東北大学工学部附属材料強度研究施設
関連論文
- P-101 木質ペレットと熱電変換素子による熱・電気の複合システムの研究(ポスター2,ポスター発表)
- 磁気光学素子を用いた新しい非破壊探傷
- 太陽光・熱複合発電システム その3
- 太陽光熱複合発電システムの開発(その2)
- 太陽光複合発電システムの開発
- 傾斜機能材料データベースの作製
- 二液式アポジエンジン用デジタルデータ処理システム
- 液酸・液水ロケットエンジン用点火器の真空着火試験
- 固体ロケット残留推力の実験
- 炭素鋼表面き裂材の腐食疲労き裂進展挙動に関する破壊力学的研究