へき開き裂発生点と破壊靱性値の寸法効果に関する研究 : 第1報,SM400C鋼の延性-脆性遷移温度領域での結果

概要

論文の詳細を見る
Fracture toughness tests were performed at -50℃ in the ductile-brittle transition temperature region for a low-strength steel SM400C using 0.3T, 0.5T, 0.8T and 1T compact specimens. All the locations of the cleavage crack initiation sites and fibrous crack shapes were investigated in detail from the fracture surface using by a scanning electron microscope and a binocular stereoscopic microscope. The probabilistic characteristics of cleavage fracture toughness and the thickness effect of cleavage crack initiation sites were analysed systematically. All cleavage crack initiation sites were found within a certain distance from the specimen surfaces. By locating all the sites and investigating fibrous crack shapes, the plane strain regions in specimens were deduced. The criterion for obtaining plane strain at the midplane of the specimens is given by B≧0.004(K_C(J)/σ_<ys>)^2+0.01. This criterion indicates the specimen thickness necessary for the plane strain condition to be fairly smaller than the size requirements in ASTM Standard E399.
社団法人日本機械学会の論文
1995-07-25