延性-脆性遷移温度領域における平面ひずみ破壊靱性の評価に関する研究 : 第3報,小形疲労試験片による評価

概要

論文の詳細を見る
Fracture toughness tests have been made in a transition temperature region at stress ratio R=-1.0 using 1TCT specimens which were cut out from SM41C carbon steel. Considerations of a plane strain fracture toughness and a plane strain condition at a brittle fracture were performed. The main results obtained were as follows. (1) The plane strain fracture toughness in the transition temperature region was simply obtained from a test which was carried out at R=-1.0 using a few small specimens. (2) A stress condition occurring in front of a crack at a brittle fracture satisfied the plane strain condition. (3) da/dN from the fatigue test data at stress ratio R=-1.0 can be extrapolated by ΔJ even in the transition temperature region. (4) The plane strain fracture toughness can be obtained from the minimum value of the fracture toughness test data using 20 three-point bend specimens in the transition temperature region.