多段多重重複繰返し応力による疲労の研究

概要

論文の詳細を見る
For the purpose of studying the progressive fatigue damage accumulation normalized V notched steel (0.36%C) specimens were subjected to experiments under the repeated stress of multifolded and multiple loading. The mechanical properties of the material of the specimens are given as follows ; tensile strength σ_B = 58.0 kg/mm^2, lower yield point σ_S = 30.4 kg/mm^2, actual breaking point σ_T = 91.5 kg/mm^2. The first experiment consisted of test of fatigue under the stress of multifolded and multiple loading of the following patterns, and the experiment was repeated until fracture was made. (1)σ_1→σ_2→σ_3→σ_2→σ_1→σ_2→……… (2) σ_2→σ_3→σ_2→σ_1→σ_2→σ_3→…… (3)σ_3→σ_2→σ_1→σ_2→σ_3→σ_2→…… where σ_1 = 15 kg/mm^2, σ_2 = 18 kg/mm^2, σ_3 = 21 kg/mm^2. It is found that the larger is the number of loading cycle by decreasing the frequency of repetition on each stress level the smaller the total sum of the cycle ratio will become, descending ultimately to approximately 0.6. Furthermore, in order to investigate the above mentioned fact, fatigue tests were conducted under the same pattern with only one loading cycle at the beginning of the loading, followed by constant stress amplitude. It appears that the total sum of the cycle ratios is much affected by the stress change at the beginning of the loading.
社団法人日本材料学会の論文
1965-11-15