高マンガン鋼の疲労強度と微視的き裂の発生

概要

論文の詳細を見る
Fatigue behavior of high manganese non-magnetic austenitic steel (HM steel) was studied through the rotating bending fatigue tests using plain specimens with a partial shallow notch by means of the successive-taken replica method. This behavior was compared with that of an austenitic stainless steel (SUS304). The experimental results showed that the fatigue limit of HM steel was the same as that of SU304, and distinct knee point was observed in S-N curve of both mateerials. It was found that the fatigue cracks of these materials initiated at grain boundaries or in its neighborhood. It was apparently observed that some non-propagating micro-cracks existed in the specimen surface of HM steel subjected to the stress cycling of fatigue limit by 10^7 cycles, while no micro-crack existed in the specimen of SUS304 subjected to the same stress condition.
社団法人日本材料学会の論文
1994-03-15