回転曲げ疲労試験中におけるX線を用いた実応力分布測定(<特集>X線材料強度)

概要

論文の詳細を見る
The purpose of this investigation is to detect a damage from actual stress distribution in the surface of specimen by using X-ray diffraction technique during fatigue test. An apparatus to measure actual stress distribution along circumference of specimen was fabricated by use of a cantilever type rotary bending fatigue machine and a stress analyzer based on single exposure technique with two position sensitive proportional counters. We proposed a method to collect separately the diffraction profile at each position along circumference of specimen. Actual stress distributions at the maximum tensile applied stress were measured during fatigue test. As results, the shape of actual stress distribution was keeping stable with increasing number of cycles until crack initiation. After crack initiation, the actual stress at the position of crack initiation was decreased suddenly near 0 MPa, and the distribution was shaped "V" type. The "V" type distribution was appeared when crack length reached greater in size than a width of irradiation area. These results show that the method proposed in this study is available to detect a position and period of crack initiation.
社団法人日本材料学会の論文
1999-07-15