溶液反応及び水熱反応法によるバーネサイト型ナトリウムマンガン酸化物の合成

概要

論文の詳細を見る
A birnessite-type sodium manganese oxide with a layered structure was synthesized by the reaction of Mn(NO_3)_2 solution with a mixed solution of H_2O_2 and NaOH at room temperature. This sodium manganese oxide was hydrothermally treated in neutral, acidic and alkaline solutions at 150°C. The original samples which were synthesized at room temperature and hydrothermally treated samples were characterized by XRD, DTA-TG, FT-IR spectroscopy and chemical analysis. The formation of the birnessite-type sodium manganese oxide is dependent on the mixed mole ratio of NaOH/Mn(NO_3)_2. The fraction of the birnessite phase increased with increase in mixed mole ratio of NaOH/Mn(NO_3)_2. The birnessite-type manganese oxide has a basal spacing of 1.004 nm before air-drying, but it changes to 0.724 nm after the air-drying at room temperature. A well crystallized birnessite phase with a basal spacing of 0.724 nm was obtained by hydrothermally treating the birnessite-type sodium manganese oxide prepared at room temperature with a NaOH solution.
社団法人日本セラミックス協会の論文
1997-07-01