NEAR-THRESHOLD PROPAGATION OF DELAMINATION FATIGUE CRACKS IN UNIDIRECTIONAL CF/PEEK LAMINATES IN AIR AND IN WATER
スポンサーリンク
概要
- 論文の詳細を見る
The effects of stress ratio and a water environment of the near-threshold growth of delanimation fatigue cracks were investigated with unidirectional laminates made from ICI APC-2 thermoplastic prepregs(AS4/PEEK). Tests were carried out under mode I opening loading by using double cantilever beam specimens. The fatigue crack growth rate near the threshold region was mainly controlled by the stress intensity range rather than the maximum energy release rate and the energy release rate range. The fatigue crack growth resistance of AS4/PEEK laminates was much higher than that of conventional CF/epoxy laminates even near the threshold region. However, the increase in fatigue resistance was smaller than that in fracture toughness. Tests in water did not show large detrimental effects. The crack propagation rate in water was expressed as two power functions of the energy release rate range. The exponent of the power function in the low propagation rate region was smaller than that in the high propagation rate region, and the growth threshold was not observed. The mechanism of the existence of the two power functions was discussed by conducting tests in water at lower frequency of stress cycling. Mesoscopic mechanism of delamination fatigue crack growth in air and in water was discussed on the basis of the fractographic observation.
- 社団法人日本材料学会の論文
- 1995-06-15
著者
-
TANAKA Keisuke
Department of Mathematical and Computing Sciences, Tokyo Institute of Technology
-
Ochiai Shojiro
Mesoscopic Materials Research Center Faculty Of Engineering Kyoto University
-
HOJO Masaki
Mesoscopic Materials Research Center, Graduate School of Engineering, Kyoto University
-
Tanaka Keisuke
Department Of Cardiovascular Surgery Nagoya Daini Red Cross Hospital
-
Hojo Masaki
Mesoscopic Materials Research Center Faculty Of Engineering Kyoto University
-
Tanaka Keisuke
Department Of Mechanical Engineering Nagoya University
-
Tanaka Keisuke
Department Of Biochemistry Faculty Of Veterinary Medicine Hokkaido University
-
Tanaka Keisuke
Department Of Applied Chemistry Waseda University
関連論文
- Key Generation for Fast Inversion of the Paillier Encryption Function
- High Space-Resolutive Evaluation of Subsurface Stress Distribution by Strain Scanning Method with Analyzer Using High-Energy Synchrotron X-Rays(Macro-, Micro-, Meso-, and Nano-scopic Strength of Materials Relating to Microstructures)
- 2P-278 シアノバクテリアの青色光受容タンパク質SyPixDの構造変化の時間分解検出(光生物・視覚,光受容(2),第46回日本生物物理学会年会)
- 3P276 青色光センサータンパク質PixDとレスポンスレギュレーターPixEのタンパク質問相互作用の時間分解観測(光生物-視覚・光受容,第48回日本生物物理学会年会)
- Effect of Interface Control on Inplane and Interlaminar Fracture Behavior of C/C Composites(Composite 4)
- Effect of Interface Control on Mode I Interlaminar Fracture Toughness of Woven C/C Composite Laminates
- Effects of Interface Control and Heat-Treatment Temperature on Interlaminar Shear Strength and Mode II Interlaminar Fracture Toughness of Woven C/C Composites
- Simulation Study on Influences of Damage-Induced Mechanical Interactions, Residual Stresses and Interfacial Frictional Shear Stress on Interfacial Debonding in Multifilamentary composites
- Approximate Solution of Interactions among Spatially Distributed Broken Fiber, Matrix and Interface in the Progress of Interfacial Debonding in Multifilamentary Unidirectional Composites
- Effect of Water Environment on Mode II Delamination Fatigue in Interlayer-Toughened CFRP
- The influence of thermal residual stresses on the transverse strength of CFRP under tensile load using FEM
- Yield Criteria for Polymers in Composite-Like Stress State
- X-Ray Study of Mechanical Properties of TiN Thin Films Coated on Steel by Ion Beam Mixing Method
- X-Ray Study of Mechanical Properties of TiN Films Coated on Steel by Ion Beam Mixing(Thin Films)
- X-Ray Stress Measurement of Hexagonal Polycrystals with[001]Fiber Texture
- Calculation of Stress Concentration at the Edge of Island Layer: Demonstration for GaAs/Si
- Shuffle for Paillier's Encryption Scheme(Discrete Mathematics and Its Applications)
- 1P-222 青色光センサータンパク質PixDの光誘起構造変化および分子間相互作用変化の研究(光生物-視覚・光受容,第47回日本生物物理学会年会)
- 1P-061 光センサータンパク質TePixDの反応ダイナミクスへの圧力効果(蛋白質-機能(反応機構,生物活性など),第47回日本生物物理学会年会)
- Effect of Cracks on Stress Reduction in GaAs/Si Heterostructures
- Fatigue Mechanisms of Porous Silicon Carbide under Cyclic Loading(Ceramics & Rocks 1)
- Primitive Power Roots of Unity and Its Application to Encryption
- Schemes for Encryption with Anonymity and Ring Signature(Public Key Cryptography, Cryptography and Information Security)
- Simulation Study for Temperature-Dependence of Tensile Strength of Continuous and Discontinuous Unidirectionally Fiber-Reinforced Metal Matrix Composites
- Neutron Diffraction Study of Thermal Residual Stress in Ceramic Composite
- Less Invasive Surgical Closure of Patent Ductus Arteriosus in Extremely Low Birth Weight Infants
- Successful Repair of Supravalvular Aortic Stenosis with Ostial Stenosis of the Left Coronary Artery using Brom's Three Patch Technique
- Detection Rates of TT Virus DNA in Serum of Umbilical Cord Blood, Breast Milk and Saliva
- 3P087 青色光受容BLUFタンパク質TePixDの光反応生成物の決定(蛋白質-機能(反応機構,生物活性など),第48回日本生物物理学会年会)
- NEAR-THRESHOLD PROPAGATION OF DELAMINATION FATIGUE CRACKS IN UNIDIRECTIONAL CF/PEEK LAMINATES IN AIR AND IN WATER
- RATE-DEPENDENT MODE II INTERLAMINAR FRACTURE BEHAVIOR OF CARBON-FIBER/EPOXY COMPOSITE LAMINATES
- DS-1-1 Variations on Pseudo-Free Groups
- Recovery of postural stability following conscious sedation with midazolam in the elderly
- Roles of Cation and Anion Molecules in Ferridistortive Phase Transition in [A(CH_3)_4]_2XBr_4 Type Crystals
- Key Generation for Fast Inversion of the Paillier Encryption Function
- Fatigue Strength Evaluation of Cracked Components
- X-Ray Study on Lattice Strain and Domain Switching Induced in Rhombohedral PZT by Poling and External Loading
- Deformation and Fracture of Piezoelectric Ceramics(Student Poster Session)
- Local Stress Measurement in Notched Sapphire by Raman Microspectroscopy
- Single Crystal Elastic Constants of β-Silicon Nitride Determined by X-Ray Powder Diffraction
- Lattice Strain and Domain Switching Induced in Tetragonal PZT by Poling and Mechanical Loading
- Elastic Constants and X-Ray Stress Measurement of Cubic Thin Films with Fiber Texture
- X-Ray Measurement of Residual Stress in Patterned Aluminum Thin Films Sputtered on Silicon Wafers
- Propagation of Delamination Fatigue Cracks in CFRP in Water
- Symmetricity of the Protocols Related to Oblivious Transfer
- RESIDUAL STRESS OF ALUMINUM THIN FILMS MEASURED BY X-RAY AND CURVATURE METHODS
- Estimation of Spalling Stress in Thermal Barrier Coatings Using Hard Synchrotron X-Rays
- Ferridistortive Phase Transition in [N (CH_3)_4]_2CoBr_4 Crystals
- Fatigue Crack Initiation Behavior in Ultrafine-Grained Steel Observed by AFM and EBSP(Advanced Technology of Experimental Mechanics)
- Evaluation of Fracture Toughness of Porous Ceramics
- Conditional Converge Cast
- X-Ray Stress Measurement of TiN Thin Film with Fiber Texture under External Loading
- Prediction of Propagation Path of Matrix Cracks in FRP under Remote Mode I Loading(Composite 3)
- Transition from Small to Large Interlaminar Cracks in Fiber-Reinforced Laminated Composites
- Porosity Effect on X-Ray Elastic Constants of Sintered Ceramics
- Fracture mechanism of cross-ply carbon/carbon composites
- An Efficient Anonymous Group Identification Scheme with Short Secret Keys(Information Security)
- Notch-Plasticity Effect on Closure of Short Fatigue Cracks
- Notch-Root-Radius Effect on Propagation of Short Fatigue Cracks in Notched Specimens of Low-Carbon Steel : Series A : Solid-Mechanics, Strength of Materials
- Neutron Diffraction Measurements of Residual Stresses in Engineering Materials and Components(Materials Evaluation by X-ray and Neutron Diffractions)
- Evaluation of Fatigue Damage in SiCp/2024Al Composite by X-Ray Method(Composite 1)
- Ferroelasticity in [P(CH_3)_4]_2CoBr_4 Single Crystals
- DS-1-3 A Compact Signature Scheme with Ideal Lattice (Extended Abstract)
- A Cramer-Shoup Variant Related to the Quadratic Residuosity Problem(Public Key Cryptography, Cryptography and Information Security)
- Mechanisms and Mechanics of Short Fatigue Crack Propagation
- Density Attack to the Knapsack Cryptosystems with Enumerative Source Encoding(Information Security)
- Catalytic Oxidative Coupling of Methane Assisted by Electric Power over a Semiconductor Catalyst
- A Method for Prediction of Fatigue Limts of Notched Members
- A Multi-Trapdoor Commitment Scheme from the RSA Assumption
- PURIFICATION OF OVIDUCTIN FROM HAMSTER OVIDUCTS AND A NEW SCREENING METHOD FOR MONOCLONAL ANTIBODIES INHIBITING SPERM-OVIDUCTIN RECOGNITION
- An Efficient Non-interactive Universally Composable String-Commitment Scheme
- Leakage-Resilience of Stateless/Stateful Public-Key Encryption from Hash Proofs
- Effect of Polarization on Deformation and Fracture of Tetragonal PZT(Materials Evaluation by X-ray and Neutron Diffractions)