Fracture mechanism of cross-ply carbon/carbon composites
スポンサーリンク
概要
著者
-
Ochiai Shojiro
Mesoscopic Materials Research Center Faculty Of Engineering Kyoto University
-
Hojo Masaki
Mesoscopic Materials Research Center Faculty Of Engineering Kyoto University
-
TAKAHASHI Jun
National Institute of Materials and Chemical Research, AIST, MITI, Department of Composite Materials
-
JOYAMA Nobuhiro
Mesoscopic Materials Research Center, Faculty of Engineering, Kyoto University
-
Joyama Nobuhiro
Mesoscopic Materials Research Center Faculty Of Engineering Kyoto University
-
Takahashi Jun
National Institute Of Materials And Chemical Research
-
Takahashi Jun
National Institute Of Materials And Chemical Research Aist
関連論文
- Effect of Interface Control on Inplane and Interlaminar Fracture Behavior of C/C Composites(Composite 4)
- Effect of Interface Control on Mode I Interlaminar Fracture Toughness of Woven C/C Composite Laminates
- Effects of Interface Control and Heat-Treatment Temperature on Interlaminar Shear Strength and Mode II Interlaminar Fracture Toughness of Woven C/C Composites
- Simulation Study on Influences of Damage-Induced Mechanical Interactions, Residual Stresses and Interfacial Frictional Shear Stress on Interfacial Debonding in Multifilamentary composites
- Approximate Solution of Interactions among Spatially Distributed Broken Fiber, Matrix and Interface in the Progress of Interfacial Debonding in Multifilamentary Unidirectional Composites
- Effect of Water Environment on Mode II Delamination Fatigue in Interlayer-Toughened CFRP
- The influence of thermal residual stresses on the transverse strength of CFRP under tensile load using FEM
- Yield Criteria for Polymers in Composite-Like Stress State
- Calculation of Stress Concentration at the Edge of Island Layer: Demonstration for GaAs/Si
- Effect of Cracks on Stress Reduction in GaAs/Si Heterostructures
- Simulation Study for Temperature-Dependence of Tensile Strength of Continuous and Discontinuous Unidirectionally Fiber-Reinforced Metal Matrix Composites
- NEAR-THRESHOLD PROPAGATION OF DELAMINATION FATIGUE CRACKS IN UNIDIRECTIONAL CF/PEEK LAMINATES IN AIR AND IN WATER
- RATE-DEPENDENT MODE II INTERLAMINAR FRACTURE BEHAVIOR OF CARBON-FIBER/EPOXY COMPOSITE LAMINATES
- Development of ultra-high temperature testing equipment and some mechanical and thermal properties of advanced carbon/carbon composites
- Enantioselective Microbial Oxidation of Allyl Alcohols
- Asymmetric Reduction of α, β-Unsaturated Cyclic Ketones by a Yeast
- Fracture mechanism of cross-ply carbon/carbon composites
- The influence of thermal shock on inter-laminar shearing strength of woven C/C composites