高温域における球形コークスの反応にともなう組織変化と粉発生挙動(コークス)(<特集>製銑プロセスの機能強化と新展開)

概要

論文の詳細を見る
According to the pulverized coal injection (PCI) into blast furnace (BF), the fine generation of coke in the lower part of BF especially around raceway has come to an important problem for stable operation. In this study, three kind of spherical cokes were used for gasification experiment simulated to the lower part of BF (1500-1700℃). Each cokes before and after experiments were examined the fine generation using I type tumbler for single particle which was developed by authors. The behavior of fine generation in high temperature can not predict from the conventional industrial tests such as CSR, DI, CRI and JIS-RI, because the industrial tests are carried out around 1000℃ and the apparent reaction rate of coke consist of not only a chemical reaction rate but also a diffusion of gas in pore, depending on the reaction temperature. Especially in higher temperature than 1500℃, graphitization behavior will affect significantly on the apparent reaction rate. Then, structure change of coke after experiment was investigated using fluorescent resin and the change of porosity from the surface was clarified. The reaction zone from the surface to the inside was determined by computer aided image analysis. It was found that the amount of coke remained in the reaction zone was in good agreement with that of fine generated from coke.
社団法人日本鉄鋼協会の論文
2001-05-01