α+γ二相域で均熱後オーステンパー処理した 0.4%C-Si-1.2%Mn 鋼の残留オーステナイト

概要

論文の詳細を見る
To clarify the formation process of the retained austenite in 0.4%C-Si-1.2%Mn steel intercritically annealed followed by austempering, changes in fraction of reained austenite (V_γ), solute carbon content in retained austenite (C_γ) and microstructure with isothermal holding time at 350∿450℃ were examined by X-ray diffraction measurement and electron microscopic observation. It was concluded that blocky retained austenite grains with less than 2∿3μm dia. found in the above steel and the interlath retained austenite films having been reported by others in the higher carbon (≧0.6C)-Si-Mn steel annealed at single austenite range and austempered, were the same in chemical stability of austenite by carbon enrichment, in spite of differences in site and morphology. Formation of blocky retained austenite may be attributed to the smaller austenite grain size obtained by cold rolling and intercritical annealing. Addition of Si may cause decreasing of carbide precipitation and increasing V_γ at the holding time the maximum of C_γ(C_<γmax>) is reached, with C_<γmax> unchanged.
社団法人日本鉄鋼協会の論文
1991-08-01