溶融鑛滓の粘性 (I) : CaO-SiO_2-Al_2O_3 系の粘性§
スポンサーリンク
概要
- 論文の詳細を見る
Viscosity of Synthetic CaO-SiO_2-Al_2O_3 slags was measured by rotating an inner-cylinder viscosimeter. Iso-viscosity lines at 1, 500 and 1, 600℃ were plotted on the diagram. Viscosity of CaO-SiO_2 slags at 1, 600℃ increased with SiO_2 content; and anomaly was not found at the composition corresponding to CaO.SiO_2. By a small amount of Al_2O_3 added to CaO-SiO_2 slag the viscosity was almost unaffected, but at more than 20% Al_2O_3 increase of the viscosity became remarkable. Viscosity of the CaO-Al_2O_3 side slags which had never been determined were found rather low and comparable to the low viscosity region in the CaO-SiO_2 side slags. And some considerations on structures of these molten slags were given from the experimental results.
- 社団法人日本鉄鋼協会の論文
著者
関連論文
- 金屬合金の眞空熔解に關する展望
- 上注ぎ造塊時のスプラッシに関する基礎的研究
- 63 上注ぎ造塊時のスプラッシに関する基礎的研究(製鋼・平炉, 日本鉄鋼協会第 62 回(秋季)講演大会)
- 鉄-硫黄-珪素合金の真空熔解に関する実験
- 熔鉄中における珪素の拡散(第2報)
- 純鐵の眞空熔解に關する熱力學的考察
- 軟β線の自己吸収の一測定法
- 熔融CaO-SiO2-Al2O3鉱滓中の硫黄の拡散
- 放射性同位元素による金属工学(主に鉄冶金学)の研究
- 溶融鑛滓の粘性 (II) : CaO-SiO_2-Al_2O_3-MgO 系の粘性