生体用β型Ti-29Nb-13Ta-4.6Zr合金の熱処理プロセスと力学的性質

概要

論文の詳細を見る
Practical size ingot of new β-type titanium alloy, Ti-29Nb-13Ta-4.6Zr, which was composed of non-toxic elements of Nb, Ta and Zr, with lower modulus of elasticity, high strength and excellent biocompatibility was tried to be fabricated. Then the heat treatment processes of the alloy, which gave a good balance of strength, ductility and modulus of elasticity, were investigated in this study. Practical size ingot of Ti-29Nb-13Ta-4.6Zr with a weight of 17kg has been successfully fabricated. The distribution of alloying elements was homogeneous through the ingot. The practical size ingot can be easily hot forged and cold rolled by a total reduction of 98%. Ti-29Nb-13Ta-4.6Zr which was aged after cold rolling indicates higher strength and lower elongation as compared with those of the alloy aged after solution treatment. In the aging temperature range between 598K and 648K, the alloy indicates relatively higher strength and lower elongation. The precipitation of ω phase increases tensile strength and decreases elongation in the alloy aged between 598K and 643K after solution treatment. In the aging temperature above 673K, the precipitation of α phase increases tensile strength and elongation in the alloy aged after solution treatment. New alloy has excellent strength ductility relationship when aging temperature was above 673K.
社団法人日本鉄鋼協会の論文