THE MINI-COLUMN OF LANTHANUM TREATED HYDROXYAPATITE CERAMIC BEADS FOR HIGH PERFORMANCE LIQUID CHROMATOGRAPHY OF PROTEIN

概要

論文の詳細を見る
Lanthanum treated hydroxyapatite (La-HAP) beads was prepared and applied for the high performance liquid chromatography (HPLC). X-ray analysis of lanthanum on La-HAP was performed. Appearance of La-HAP beads was also observed by a scanning electron microscope. After the treatment of the HAP beads with the lanthanum chloride solution, the small fluffy structure on the surface of beads and then some inside fiber-like structure were observed. The elution behavior on La-HAP mini-column (0.76 I. D. ×0.4cm) was compared with those of HAP mini-column (0.76 I. D. ×0.4cm). Proteins were loaded on a column and eluted by liner gradient system. The relationship between capacity factor (k') of various proteins on La-HAP column and k' on HAP was estimated through the correlation coefficient as 0.93. The elution pattern of proteins on La-HAP column was approximately similar with that on HAP, but the adsorption of proteins on La-HAP was a little stronger than on HAP. After chromatography under acidic conditions, La-HAP beads were observed by electron microscope again. Fiber-like structure remained even after fifty cycles of chromatography. The height equivalent to a theoretical plate number (HETP) was estimated with tryptophan (0.25μg/5μl) in isocratic elution system (pH4.0). The change of HETP by prolonged use under acidic conditions was determined. Half height width of tryptophan peak on La-HAP (approximately 0.5mm) was persistent for 120min and after 120min gradually increased. While under the same conditions, HETP on HAP was remained only for about 40min. The durability of La-HAP seemed to be as three times as larger than that of HAP. It should be studied further that the results described above simply imply whether one-third of surface area of HAP is covered by lanthanum, or the durability of this material under acidic conditions is improved actually. According to the results of chromatography, the treatment with lanthanum chloride solution may not be homogeneous, and the improvement of processing of lanthanum coating of HAP is also remained to be studied. And then, so far studied, lanthanum-hydroxyapatite would be useful for the packing material for HPLC for separation of proteins and other biomacromolecules under fairly acidic conditions even.
神奈川歯科大学の論文
1994-12-25

THE MINI-COLUMN OF LANTHANUM TREATED HYDROXYAPATITE CERAMIC BEADS FOR HIGH PERFORMANCE LIQUID CHROMATOGRAPHY OF PROTEIN

スポンサーリンク

概要

著者

関連論文

スポンサーリンク