鉛フリーハンダをダイヤモンド砥粒固定材に用いたソーワイヤの開発とそれを用いたサファイヤインゴットのスライス加工への適用
スポンサーリンク
概要
- 論文の詳細を見る
We produced the diamond saw wire using the commercial lead-free solder as a fixing material of diamond abrasive particles, and sliced sapphire ingots into wafers with the saw wires.<BR>The co-drawn brass coated piano wire was adopted as a core material. Electroless Ni-P coated diamond abrasive particles were employed to enhance adhesion between the solder and diamond abrasive particle. We developed the equipment that performs solder coating on wire, temporary fitting of diamond abrasive particles on wire, and final fixing, in one continuous operation. We were able to produce saw wires as long as around 2 km. By using these saw wires we succeeded in slicing a sapphire ingot of 50.8 mm diameter into 50 wafers at a time. However, the average thickness of the wafers tended to be thinner toward the winding side of the wire saw machine. The total thickness variation (TTV), the maximum surface waviness (WT) and the maximum surface roughness (RZ) tended to increase toward the winding side. During the slicing process of ingot, the load on the saw wire maximized when the wire had moved a considerable distance away from the center of the ingot.
- 2012-05-15
著者
-
中平 敦
大阪府立大学・マテリアル工学分野
-
中平 敦
大阪府立大学
-
村田 安規
(株)中村超硬
-
井上 誠
(株)中村超硬
-
横田 勝
(株)中村超硬
-
大谷 靖彦
日本ノズル(株)
-
島田 英明
(株)中村超硬
-
冨吉 努
(株)中村超硬
-
井上 紘章
(株)中村超硬
関連論文
- 磁場を用いた骨再生の検討
- ダイヤモンドワイヤーソー高性能化のための低融点コート材の開発: 機械的性質に及ぼすNi添加の影響
- P103 ナノ材料の安全性評価手法探索
- 水熱法によるH-Ti-Oナノチューブ合成と構造評価(セラミック材料)
- 水熱合成HTiOナノチューブの構造評価と特性 (特集 触媒および光触媒材料の分子レベルでの理解(2))
- 617 新規HTioナノチューブの合成とその評価(ナノ材料の特性評価I, 最先端のナノマテリアル)
- ナノチューブ状HTiOの合成と構造評価 (特集 酸化物ナノチューブの最近の進展)
- Ag-Cu-Sn合金の低温ろう付け特性と機械的性質
- 低融点ろう材によるダイヤモンド砥粒固定ワイヤーソーの試作とこれを用いた単結晶シリコンのスライス加工
- 高勾配磁気分離法による染料分子回収法の開発