Fabrication of Ultra High Nitrogen Austenitic Stainless Steel by NH_3 Solution Nitriding
スポンサーリンク
概要
- 論文の詳細を見る
Nitrogen addition to stainless steels is very effective for improving mechanical properties and corrosion resistance. N2 solution nitriding is one of the possible methods to produce high nitrogen stainless steel. However, the nitriding rate by N2 gas is significantly small and also the attainable nitrogen contents in Fe–Cr alloys is less than 1 mass% in general. NH3 nitriding is an attractive alternative since NH3–H2 gas mixtures have high corresponding nitrogen potential than that of pure N2 gas.In the present study, aiming for the enhancement of the nitriding rate and the increase of nitrogen contents more than 1 mass%, NH3 and N2 solution nitriding of Fe–Cr alloys under various conditions has been carried out and their behaviors of nitrogen absorption in Fe–Cr alloys are investigated. It is found that the suppression of the pre-decomposition of NH3 before it reaches the sample is critical for the effective NH3 nitriding. Compared with the N contents after 1 h nitriding, NH3 nitriding is found to be about 5 times faster than that of N2 (0.1 MPa) nitriding under the present experimental conditions. In addition the N contents more than 1 mass% were easily achieved by NH3 nitriding. By using devised NH3 gas injection system to minimize the pre-decomposition of NH3 gas, austenitic Fe–23.5Cr alloys with more than 3 mass% of nitrogen (ultra high nitrogen stainless steel) that had never been achieved by solution nitriding was successfully produced.
- 社団法人 日本鉄鋼協会の論文
- 2010-11-15
著者
-
Sasaki Yasushi
Graduate Inst. Of Ferrous Technol. (gift) Pohang Univ. Of Sci. And Technol. (postech)
-
Jung Sung-mo
Graduate Inst. Of Ferrous Technol. (gift) Pohang Univ. Of Sci. And Technol. (postech)
-
Park Woo-il
Graduate Institute Of Ferrous Technology (gift) Pohang University Of Science And Technology (postech
-
Jung Sung-mo
Graduate Institute Of Ferrous Technology (gift) Pohang University Of Science And Technology (postech
-
Sasaki Yasushi
Graduate Institute Of Ferrous Technology (gift) Pohang University Of Science And Technology (postech
関連論文
- Bubble Formation Frequency at a Single-hole Nozzle Immersed in a Mercury Bath
- Prediction of the Occurrence of Swirling Liquid Jet Generated by Off-centered Nozzle
- The Coordination of F Ions around Mg and Ca Ions in Molten CaO–CaF2–MgO–SiO2 System at 1873K
- EFFECT OF LOW-DENSITY PARTICLES ON SWIRLING LIQUID JET IN TRANSIENT PERIOD
- The Coordination of F Ions around Al and Ca Ions in Molten Aluminosilicate Systems
- The Role of Ca and Na Ions in the Effect of F Ion on Silicate Polymerization in Molten Silicate System
- The Estimation of the Iso-viscosity Lines in Molten CaF2–CaO–SiO2 System
- Occurrence Condition of a Swirling Bubbling Jet in a Water Bath Covered with an Oil Layer
- Stress Relaxation Behavior with Molten CaO-SiO_2-Al_2O_3 Slag
- The Effect of Grain Boundaries on the Surface Rearrangement during Wustite Reduction within its Range of Existence
- Measuring Strains for Hematite Phase in Sinter by Electron Backscattering Diffraction Method
- The Effect of Grain Boundaries on Iron Nucleation during Wustite Reduction Process
- Rupture Phenomena of Molten Alkali Silicate Thin Films
- Rupture phenomena of molten alkali silicate thinfilms
- The Role of Molten Slag in Iron Melting Process for the Direct Contact Carburization: Wetting and Separation
- Simulation of Effect of Pore Structure on Coke Strength Using 3-dimensional Discrete Element Method
- Reply to “Discussion on the Estimation of the Iso-viscosity Lines in Molten CaF2–CaO–SiO2 System”
- The Surface Structure Correlation with the Wustite Surface Rearrangement
- The Effect of Grain Boundary on the Wustite Reduction Process
- The Surface Structure Correlations with the Iron Nucleation in the Wustite Reduction
- The Surface Structure Correlations with Wustite Reduction Mechanism
- Thermodynamic Study on Redox Equilibrium of Manganese in CaO-SiO_2-Mn_tO-MgO_
- Effect of Initial Acceleration History on Transition to Turbulence in Pipe Flow
- Equilibria of Manganese and Sulfur between Liquid Iron and CaO-SiO_2-Fe_tO-MgO-MnO Slags Saturated with 2CaO・SiO_2 and MgO
- Thermodynamic Properties of Manganese Oxide in BOF Slags
- Empirical Equations for Bubble Formation Frequency from Downward-Facing Nozzle with and without Rotating Flow Effects
- Raman Spectroscopic Analysis of Molten Na_2O-NaCl-SiO_2 System
- Dry-Etching Characteristics of Attenuated Phase-Shifting Masks using C1_2/CF_4/O_2/He Plasmas
- Quantitative Chemical Analysis of Fluorine in the Slags Produced in Stainless Argon-Oxygen Decarburization Process by X-ray Fluorescence Spectrometry
- Viscosity of Highly Basic Slags
- Kinetic Study on Surface Dissolution of Nitrogen on Liquid Steel by Isotope Exchange Technique
- Carburization Degree of Iron Nugget Produced by Rapid Heating of Powdery Iron, Iron Oxide in Slag and Carbon Mixture
- Chemical Reaction of Glazed Refractory with Al-deoxidized Molten Steel
- Simulation Test for Crystallization of Inclusions in Semi-killed Steels during Heat Treatment Prior to Hot Rolling
- Solubility of MgO in CaO-SiO_2-MnO Slags
- Solubility of MgO in New Ironmaking Process-typed Slags
- Activity Coefficient of Manganese in Copper
- Repulsive Capillary Force between two Plates Linked by a Concave Molten Slag Bridge
- Ejection of small sedimentary particles into a cylindrical bath by swirl motion of bubbling jet (特集 流動の可視化)
- Prediction of Argon Gas Attachment to Sliding Gate in Immersion Nozzle
- Forward and Backward Reaction Rate Constants of the Reaction of C+O=CO (g) on Fe-C Melts
- Enhancement of Iron Melting Rate under the Co-existence of Graphite and Wustite
- Molecular dynamics analysis of the effect of F on the structure of molten Na_2O-NaF-Al_2O_3-SiO_2 system
- Molecular Dynamics Analysis of Three-dimensional Anionic Structures of Molten Al_2O_3-Na_2O-SiO_2 System
- Thermodynamics of Titanium Oxide in Ladle Slags
- Simulation of Effect of Pore Structure on Coke Strength Using 3-dimensional Discrete Element Method
- Chemical Analysis of Zinc Electroplating Solutions by X-ray Fluorescence Spectrometry
- The Role of Molten Slag in Iron Melting Process for the Direct Contact Carburization : Wetting and Separation
- Chemical Reaction of Glazed Refractory with Al-deoxidized and Ca-treated Molten Steel
- Formation of Calcium Ferrites under Controlled Oxygen Potentials at 1273K
- Fabrication of Ultra High Nitrogen Austenitic Stainless Steel by NH_3 Solution Nitriding
- Carbonation Reaction of CaO in Jet Milling of CO_2 Gas
- The effect of Fe_tO Content on MgO Solubilities in Lime-based Slags
- The Role of Iron Oxide Bearing Molten Slag in Iron Melting Process for the Direct Contact Carburization
- The Coordination of F Ions around Mg and Ca Ions in Molten CaO-CaF_2-MgO-SiO_2 System at 1873K
- Prediction of the Period of Swirl Motion Appearing in Gas Injection Processes at High Temperatures
- Mixing Time in a Bath in the Presence of Swirl Motion Induced by Horizontal Gas Injection with an L-Shaped Lance
- Effect of Repeatedly Imposed Acceleration on the Transition to Turbulence in Transient Circular Pipe Flow
- Model study of the effect of slag layer on the swirl motion of molten steel jet (環境特集号(その1))
- Grain Refinement of α-iron by Repeated Carburizing and Decarburizing Reactions
- Data Arrangement and Consideration of Evaluation Standard for Silico-Ferrite of Calcium and Alminum (SFCA) Phase in Sintering Process
- Feasibility of Solid-state Steelmaking from Cast Iron : Decarburization of Rapidly Solidified Cast Iron
- Mixing Time in a Cylindrical Bath Agitated by Gas Injection through an L-shaped Top Lance in the Absence of Swirl Motion
- Morphologies of Alumina Nano- and Microparticles at the Fe/Al2O3 Interface and the Effects of Reaction Time and Substrate Roughness on Size Distribution
- A Kinetic Study on Carburization of Fe by Using 13CO Isotope Gas
- Enhanced Carburization of Iron by CH4-containing Gas at 1573 K
- Metal-slag Separation Behaviors of Pellets Consisted of Iron, Graphite and CaO–Al2O3 Based Slag Powders