Effect of preliminary irradiation on the bond strength between a veneering composite and alloy
スポンサーリンク
概要
- 論文の詳細を見る
The shear bond strength of a veneering composite (Solidex) and silver-palladium-copper-gold alloy (Castwell M.C.12) was evaluated for different duration times and irradiance for preliminary photo-polymerization. A veneering composite was applied onto a cast disk. Preliminary photo irradiation was performed using different duration times or irradiance. After final polymerization, the bond strength and the spectral distribution of each curing unit were determined. Shear bond strength was significantly higher for 90 s (12.4 MPa), than that for 0 s (8.3 MPa). With regard to the effect of irradiance, that from Solidilite (11.4 MPa) was significantly higher than that from Sublite S at 3 cm (8.7 MPa). The irradiance of Hyper LII and Sublite S at 3 cm was higher than Sublite S at 15 cm or Solidilite unit. Long time irradiation and low intensity is effective for preliminary irradiation in order to enhance the bond strength.
- 2010-01-01
著者
-
MATSUMOTO Yoshifumi
Nihon University Graduate School of Dentistry
-
FURUCHI Mika
Department of Fixed Prosthodontics, Nihon University School of Dentistry
-
OSHIMA Akiko
General Practice Residency, Nihon University School of Dentistry Dental Hospital
-
TANOUE Naomi
Nagasaki University Hospital
-
KOIZUMI Hiroyasu
Department of Fixed Prosthodontics, Nihon University School of Dentistry
-
MATSUMURA Hideo
Department of Fixed Prosthodontics, Nihon University School of Dentistry
-
Matsumoto Yoshifumi
Nihon Univ. Graduate School Of Dentistry Tokyo Jpn
-
Matsumura H
Department Of Fixed Prosthodontics Nihon University School Of Dentistry
-
Koizumi H
Department Of Fixed Prosthodontics Nihon University School Of Dentistry
-
Koizumi Hiroyasu
日本大学 歯学部
-
Tanoue N
Nagasaki University Hospital
-
Tanoue Naomi
Nagasaki Univ. Hospital Nagasaki Jpn
-
Tanoue Naomi
Division Of General Dentistry Nagasaki University Hospital
-
Matsumura Hideo
Nihon Univ. School Of Dentistry Tokyo Jpn
-
Matsumura Hideo
Department Of Fixed Prosthodontics Nihon University School Of Dentistry
-
Matsumura Hideo
Department Of Crown And Bridge Prosthodontics Nihon University School Of Dentistry
-
Furuchi Mika
Department Of Fixed Prosthodontics Nihon University School Of Dentistry
-
Oshima Akiko
General Practice Residency Nihon University School Of Dentistry Dental Hospital
-
Koizumi Hiroyasu
Department Of Fixed Prosthodontics Nihon University School Of Dentistry
関連論文
- Effect of preliminary irradiation on the bond strength between a veneering composite and alloy
- Evaluation of single liquid primers with organic sulfur compound for bonding between indirect composite material and silver-palladium-copper-gold alloy
- Effects of Monomer Composition and Original Filler Content on Filler Loading in the Resulting Centrifuged Composites
- Effect of alumina air-abrasion on mechanical bonding between an acrylic resin and casting alloys
- Bond Strength to Primed Ti-6Al-7Nb Alloy of Two Acrylic Resin Adhesives
- Color Stability of Acrylic Resin Adhesives with Different Initiation Modes
- Marginal and Internal Adaptation of Zirconium Dioxide Ceramic Copings and Crowns with Different Finish Line Designs
- Effect of preliminary irradiation on depth of cure and hardness of a veneering composite
- Comparative Evaluation of Thione and Phosphate Monomers on Bonding Gold Alloy and Ti-6Al-7Nb Alloy with Tri-n-butylborane initiated Resin
- Bond strength to bovine dentin of a composite core build-up material combined with four different bonding agents
- Effect of Metal Priming Agents on Bond Strength of Resin-modified Glass Ionomers Joined to Gold Alloy
- Effect of single-liquid priming agents on adhesive bonding to aluminum oxide of a methacrylic resin.
- Relation between Attractive Force and Keeper Surface Characteristics of Iron-neodymium-boron Magnetic Attachment Systems
- Effect of a Metal Priming Agent on Wear Resistance of Gold Alloy-indirect Composite Joint
- Depth of cure and hardness of an indirect composite polymerized with three laboratory curing units
- Effects of alumina air-abrasion and acidic priming agents on bonding between SUS XM27 steel and auto-polymerizing acrylic resin
- Effect of metal priming agents on bonding characteristics of an acrylic resin joined to SUS XM27 steel
- Effect of Acidic Primers on Bonding Three Magnetic Steel Alloys with Tri-n-butylborane Initiated Methacrylic Resin
- Properties of an Indirect Composite Material Polymerized with Two Different Laboratory Polymerizing Systems
- A New Laboratory Polymerizing Apparatus Equipped with Halogen and Metal Halide Light Sources
- Effect of metal halide light source on hardness, water sorption and solubility of indirect composite material
- Effect of noble metal adhesive systems on bonding between an indirect composite material and a gold alloy
- Fabrication of a maxillary posterior fixed partial denture with a type 4 gold alloy and a dual-polymerizing indirect composite
- A Nine-year Follow-up of a Porcelain Laminate Veneer Restoration Applied to an Adolescent with Traumatized Dentition : A Clinical Report
- International telephone code used for citizenship identification in a denture
- Application of a pre-impregnated fiber-reinforced composite in the fabrication of an indirect dowel-core
- Influence of Centrifugal Force on Filler Loading of Resin Composites
- Porcelain laminate veneer restorations bonded with a three-liquid silane bonding agent and a dual-activated luting composite
- Twenty-four Hour Bond Strength Between Layers of a Highly Loaded Indirect Composite
- Effect of Single-liquid Acidic Primers on Bonding of a Composite Luting Agent Joined to a Prefabricated Alumina Coping Material
- Effect of acidic primers on adhesive bonding of tri-n-butylborane initiated adhesive resin to alumina
- Evaluation of thiouracil-based adhesive systems for bonding cast silver-palladium-copper-gold alloy
- Effectiveness of Bonding Systems on Bonding Durability of a Prefabricated Porcelain Material
- Effect of Hydrofluoric Acid Etching on Shear Bond Strength of an Indirect Resin Composite to an Adhesive Cement
- Bending Property of Super-Elastic Ti-Ni Alloy Dental Castings with Different Heat Treatments
- Influence of Laboratory Light-curing Unit Variation on Properties of Prosthetic Composites
- Marginal Fit and Microgaps of Implant-abutment Interface with Internal Anti-rotation Configuration
- Effects of IL-6 and Soluble IL-6 Receptor on the Expression of Cartilage Matrix Proteins in Human Chondrocytes
- Research Projects on Materials and Devices Published in 2005 by Members of the Japan Prosthodontic Society : A Review
- Influence of Abutment Materials on the Resultant Color of Heat-pressed Lithium Disilicate Ceramics
- Evaluation of two dual-functional primers and a tribochemical surface modification system applied to the bonding of an indirect composite resin to metals
- Current bonding systems for resin-bonded restorations and fixed partial dentures made of silver-palladium-copper-gold alloy
- Influence of laboratory light sources on the wear characteristics of indirect composites
- Current status of zirconia-based fixed restorations
- Neuroprotective Effects of Ebselen Following Forebrain Ischemia : Involvement of Glutamate and Nitric Oxide
- Shear bond strength between an indirect composite veneering material and zirconia ceramics after thermocycling
- Significance of Differences Between Brain Temperature and Core Temperature (Delta T) During Mild Hypothermia in Patients With Diffuse Axonal Injury
- Effect of Surface Treatments on Repair Bond Strength of Aged Light Polymerizing Indirect Composites
- Color Stability of an Indirect Composite Polymerized with Two Different Laboratory Polymerization Systems
- Influence of Laboratory Procedure on Attractive Force of Magnetic Attachment Systems
- Effect of Varying Polymerization Modes on Flexural Strength of an Indirect Composite Reinforced with a Monomer-Impregnated Glass Fiber Material
- Effect of Noble Metal Conditioner on Wear Resistance of Composite-to-metal Bonded Specimens
- A Centrifugal Light-polymerizing Apparatus Designed for Preparation of Highly Filled Nano-composites
- Effect of Single-liquid Acidic Primers on Bonding of a Composite Luting Agent Joined to a Prefabricated Alumina Coping Material
- Effect of surface treatment on bond strength between an indirect composite material and a zirconia framework
- Influence of air-abrasion and subsequent heat treatment on bonding between zirconia framework material and indirect composites
- Properties of indirect composites reinforced with monomer-impregnated glass fiber
- Bonding between layering materials and zirconia frameworks
- The influence of polymerization conditions on color stability of three indirect composite materials
- External Carotid Artery Stenting and Superficial Temporal Artery to Middle Cerebral Artery Anastomosis for Internal Carotid Artery Occlusion With External Carotid Artery Severe Stenosis -Case Report-
- PARTIAL LIVER TRANSPLANTATION WITH PRIMARY REVASCULARIZATION IN DOGS:Preliminary Report On New Method And Its Theoretical Background
- A nine-year clinical case study of a resin-bonded fixed partial denture seated on the maxillary anterior teeth.
- Evaluation of a newly developed polymethyl methacrylate powder for brush-dip technique