カーボンナノコイルの低温合成
スポンサーリンク
概要
- 論文の詳細を見る
Synthesis of carbon nanocoils was carried out by the simple apparatus based on hot-filament CVD at catalyst temperatures below 450ºC. Copper was vacuum evaporated onto the nickel particles formed by scratching the poly-crystal nickel plate with sandpaper. These particles were used for the catalysts for synthesis of nanocoils. Heating was not performed at all for forming these particles. Ethanol as a carbon source was introduced into the chamber with argon gas. Synthesis was performed at atmospheric pressure. Carbon nanocoils could be synthesized at temperatures above 400ºC. The yield of nanocoils in total carbon fibers is about 80% at 400ºC. The diameter of these products decreases with the decrease of diameter of catalyst particles.
- 一般社団法人 表面技術協会の論文
- 2007-03-01
著者
関連論文
- 熱フィラメントCVD法による平板状ダイヤモンドの合成
- ダイヤモンドを陰極とした直流プラズマCVD法におけるダイヤモンド薄膜の高速合成の試み
- ダイヤモンド陰極を低温にした直流放電プラズマCVD法によるダイモンド薄膜の合成
- 常圧直流プラズマCVD法を用いたダイヤモンド薄膜の合成
- 陰極にダイヤモンドを用いた直流プラズマCVD法によるダイヤモンド薄膜の合成
- 熱フィラメントCVD法により合成されたダイヤモンド薄膜への紫外線照射による酸化の効果
- メタノールのみを用いた簡易ダイヤモンド合成装置の製作
- 29a-C-7 水蒸気に紫外線を照射した雰囲気中でのSiの低温熱酸化膜の紫外線を用いたアニール
- 紫外線照射による低温におけるシリコンの増速熱窒化
- 熱処理ナノダイヤモンド砥粒のTEM観察
- 赤外線照射加熱法と固体炭素原料を用いたカーボンナノファイバー低温合成の試み
- 熱処理したサブミクロンダイヤモンドの加工特性
- 熱処理を施したサブミクロンダイヤモンド砥粒の表面性状(セラミック材料)
- 塩素を用いた焼成ダイヤモンドの分散
- サブミクロンダイヤモンドにおける表面挙動 : 吸着酸素の影響(セラミック材料)
- 熱フィラメントCVD法による鉄基板上へのダイヤモンドの合成
- アルコールを炭素源とした熱フィラメントCVD法による単層及び二層カーボンナノチューブの合成
- 銅とニッケルの合金薄膜を触媒に用いたカーボンナノコイルの低温合成と線径制御
- カーボンナノコイルの低温合成
- 最近のダイヤモンド砥粒技術
- 化学気相成長法によるカーボンナノ材料の低温合成 ([日本工業大学]学内特別研究および国外研修に関する特集号) -- (特集 [日本工業大学]学内特別研究)
- The Effect of UV-Irradiation on Electroless Plating of Ni onto Si Wafer.
- The Effects of UV-Irradiation on Electroless Plating of Ni onto Al Substrate.