NiCuZnフェライト焼結体の低温作製とその材料特性評価
スポンサーリンク
概要
- 論文の詳細を見る
NiCuZn ferrite has been widely applied to multilayer chip inductors in recent years. While fabricating the multilayer structure of ferrite and metal alternatively, it is requested to simultaneously sinter in low temperature for the internal conductor Ag (Melting point 960°C) and ferrite materials. The purpose of this study is to fabricate the NiCuZn ferrite sintered body with high-strength and high-frequency magnetic property. The procedures are as follows: firstly, the NiCuZn ferrite powder was synthesized under a CO2 atmosphere at 500°C from the mixed doxalate which was synthesized by liquid phase deposition method from mixed metal chloride and ammonium oxalate; subsequently, a small amount of boric acid [H3BO3] was added to the powder, and then the NiCuZn ferrite powder compact was formed with Newton press and CIP methods; finally, the NiCuZn ferrite sintered body was fabricated by sintering at 900°C under a CO2 atmosphere. Through the experiments of high temperature shrinkage, evaluation of mechanical strength and magnetic property, NiCuZn ferrite fabricated by this study can present good characters on high frequency and high mechanical strength when the sintering temperature and boric acid additive are 900°C and 0.5 mass%, respectively.
- 社団法人粉体粉末冶金協会の論文
- 2006-03-15
著者
関連論文
- 20aHS-3 片支持湾曲結晶における蜃気楼干渉縞(20aHS X線・粒子線(X線),領域10(誘電体,格子欠陥,X線・粒子線,フォノン))
- DDS応用のための磁性流体に関する基礎研究
- マウス体内での磁性ナノ粒子流体の放射光による観察
- FeOx/Au/TiO_2触媒の活性化とCO酸化反応に対するH_2の促進効果
- 過剰H2中のCO選択酸化のための新触媒の開発 : -Part1- 多量のFeOx添加よPt触媒の超活性化
- 変態-熱-力学に基づく焼入れ・焼もどし過程のシミュレーションとその検証
- 328 相変態を考慮した焼入れ焼もどし過程のシミュレーションとその検証
- 腎臓内に注入した鉄・銀ナノ粒子の高輝度放射光による観察
- 肝臓,心臓の脈管系の放射光による造影
- 放射光を用いたDDSに関する考察 : 高輝度放射光施設SPring-8を用いた実験