Nanostructure Control of Barium Titanate--Potassium Niobate Nanocomplex Ceramics and Their Enhanced Ferroelectric Properties

概要

論文の詳細を見る
Barium titanate (BaTiO3,BT)--potassium niobate (KNbO3,KN) nanocomplex ceramics with various KN/BT molar ratios were prepared by a solvothermal method. From a transmission electron microscopy (TEM) observation, it was confirmed that the KN layer thickness on BT particles was controlled from 5 to 40 nm by controlling KN/BT molar ratios. Their dielectric constants were measured at room temperature and 1 MHz, and the maximum dielectric constant of 370 was measured for the BT--KN nanocomplex ceramics with a KN thickness of 22 nm. TEM observation revealed that at a KN thickness below 22 nm, the BT/KN heteroepitaxial interface was assigned as a strained interface, while at 40 nm, the interface was assigned as a relaxed one. These results suggested that the strained heteroepitaxial interface could be responsible for the enhanced dielectric properties.
2012-09-25