Ｓｏｌ‐Ｃｒｙｓｔａｌ法により合成したナノポーラスＮａＮｂＯ３粒子の微構造
スポンサーリンク
概要
- 論文の詳細を見る
Nano-porous NaNbO<SUB>3</SUB> was successfully synthesized from Na-Nb ethoxide by sol-crystal method. Structural characterization of specimens annealed at various temperatures was performed by a transmission electron microscope (TEM) and X-ray diffractometory. The single crystal of Na-Nb ethoxid was decomposed to an amorphous matrix below 473K. Small crystals were grown by heating above 573K, and the crystal sizes became larger with increasing temperature. At 673K, well crystallized NaNbO<SUB>3</SUB> grain with an orthorhombic structure (S.G. <I>Pbcm</I>) was observed. The three-dimensional image constructed by a tomography system showed that the grain had many inner-pores with a few ten nano-meter sizes. Thermal behavior of the inner-pore could be observed <I>in-situ</I> with a TEM using a heating stage during the crystallization process.
- 日本材料学会の論文
著者
関連論文
- 希土類Mn酸化物の層状ペロブスカイト構造特有の一次相転移
- アルジェリア民主人民共和国産ハロイサイトの加熱における構造変化
- Li-Nb-Ti酸化物系固溶体に及ぼす希土類元素の効果
- 高熱伝導AlNセラミックスの微構造と熱伝導メカニズム
- BeO添加による液相焼結炭化ケイ素の熱伝導性 : 微構造観察による検討(セラミック材料)
- 金微粒子分散酸化チタンインバースオパールの光学特性
- 1E06 高熱伝導窒化ケイ素の微構造解析
- 単分散シリカ懸濁液からの繊維状シリカの生成メカニズム
- 有機-無機ナノハイブリッド材料の研究開発
- 構造的観点からみたGd3RuO7の相転移
- Y-TZPセラミックのリサイクル
- 室温でゼロ膨張であるスポジューメン窒化ケイ素複合体
- 高強度を示したミリ波焼結アルミナのTEMによる微構造解析
- 2I08 新相 Sr_La_xMnO_3 (x=0.025∿0.1) の電子回折研究
- 1D01 Nd_2TiMnO_6 の電子顕微鏡観察
- 竹炭から作製したチューブ状SiCセラミックスの微構造(セラミック材料)
- アルミナ/YAG 一方向凝固材料の界面
- 酒石酸アンモニウム結晶テンプレートを用いて合成された遷移金属酸化物チューブ
- FAゼオライト-セピオライト複合吸着材の合成とその特性
- 透過型電子顕微鏡によるLn_2Mn_xM_O_7(Ln=rare earth or Y, M=Mo, Ta, Nb or W)の構造解析
- ナノ粒子から成るSiO_2繊維の創製
- インジェクション法による微粒子へのコーティング
- Injection法による複合粒子の合成
- インジェクション法による無機マテリアル粒子被覆
- TEMでなぜ原子が見えるのか
- Sol-Crystal法により合成したナノポーラスNaNbO3粒子の微構造 (特集 セラミック材料)
- Ba-NbエトキシドからBa_5Nb_4O_の結晶化過程の微構造的考察(イノベーティブセラミックス(I))
- 私たちの見ている風景
- インジェクション法による単層, 複層, 混合層被覆粒子の合成
- TiCの燃焼合成反応熱を利用したSiCの燃焼合成と燃結
- 自己燃焼高圧ホットプレス法で作製したTiC/SiC複合焼結体
- TEMでなぜ原子が見えるのか(ヘッドライン:原子をみる,あやつる)
- Ｓｏｌ‐Ｃｒｙｓｔａｌ法により合成したナノポーラスＮａＮｂＯ３粒子の微構造