熱拡散法により作製した光沢スズ-ニッケル合金皮膜の構造と物性
スポンサーリンク
概要
- 論文の詳細を見る
After nickel plating on copper substrates and tin plating on top of that, the effects of heat treatment on crystal structure, contact resistance and hardness of the double plating films were investigated. X-ray diffraction measurements showed that heating the tin/nickel double plating films at 180°C for one hour resulted in the formation of tin-nickel intermetallic compounds.The contact resistance of the double plating films increased with increasing heat treatment time at 180°C, and showed higher contact resistance than bright nickel films. In a humidity cabinet test at 60°C and 90 percent relative humidity, double plating films after heat treatment at 180°C for four hours showed lower contact resistance than did bright nickel films.The hardness of the double plating films was enhanced by heat treatment, and was greater than that of bright nickel films. The double plating films after heat treatment were similar in appearance to stainless steel, with a slightly pink color.
- 社団法人 表面技術協会の論文
著者
関連論文
- 3価の鉄イオンを含むスズー鉄合金めっき浴からの電析
- 中性水溶液系電気二重層キャパシタ用途としての活性炭/DNA複合化電極
- 電気化学処理による水溶液電気二重層キャパシタの高容量化
- 電気めっき法により作製したスズ-鉄合金めっき負極を用いた次世代リチウム二次電池
- スズ-鉄合金めっき負極を用いた次世代リチウム二次電池の作製とその充放電特性
- スズ-鉄合金めっき負極を用いた次世代リチウム二次電池
- 4-ニトロアニソ-ルから5-ニトログアヤコ-ル電解合成
- 電気二重層コンデンサーの高性能化
- 有機溶媒からの電析によるイットリウム複合酸化物の作製
- Lewis 酸を触媒として用いた NADH 類縁体によるアセトアルデヒドおよび同族体の還元反応