The coefficient of friction and the wear resistance of three types of alumina, that is, single crystals of sapphire (α-Al<SUB>2</SUB>O<SUB>3</SUB>), polycrystalline sintered alumina and sintered abrasive grits, on a dry stainless steel surface have been determined as a function of sliding speed. As the results, it is found that the wear of single and polycrystalline alumina appears to occur by both mechanisms, that are consisted of attritious wear with plastic flow over 20 m/s of sliding speed and fragmentation below 10 m/s, whereas the sintered abrasive grits are worn mostly by attrition with less wear rate even at low sliding speed, although, at high sliding speed, the wear is greatly increased with decreasing the bonding force of grains owing to high temperature during sliding. It is associated that the attritious wear in the single and polycrystalline alumina may be produced by chemical reactions occuring in the wear layer under high sliding speed. Also, the fragmentation resistance of alumina depends on crystallographic orientation such as plane of wear and rubbing directions, and existence of grain boundary, so that the wear resistance of the single crystals of sapphire under low sliding speed is less than that of the polycrystalline alumina.
- 社団法人 粉体粉末冶金協会の論文
著者
関連論文
- 超仕上における砥石の切れ味制御
- 水溶性加工液による超仕上げ : 電解インプロセスドレッシングの適用
- 低周波衝突振動を利用した硬脆材料のせん孔に関する基礎的研究
- 硬ぜい材料のマイクロ切削における塑性変形型材料除去の可能性
- 研削仕上面粗さの周期性に及ぼすドレッシング条件の影響
- マシニングセンタにおけるボールねじ熱膨張誤差の自動補正
- 測定バーによるラッピング定盤の表面形状解析
- 微小切削における切りくず生成温度(第1報) : 光ファイバ型赤外線輻射温度計による刃先温度の測定
- 光ファイバ型赤外線輻射温度計による加工温度の測定 : 温度計の特性
- MD法によるDLC薄膜の機械的特性の評価 : 圧子押込み特性の解析による硬さの評価