MNS-15 NANOSCALE FRICTION BEHAVIORS OF HIERARCHICAL SUPERHYDROPHOBIC STRUCTURE OF DIAMOND LIKE CARBON FILMS WITH VARIOUS HUMIDITY CONDITIONS(Micro/Nanosystem Science and Technology IV,Technical Program of Oral Presentations)
スポンサーリンク
概要
- 論文の詳細を見る
Superhydrophobic double roughening structure of DLC film was prepared by 2.45 GHz surface wave-excited plasma CVD with the mixture of methane (CH_4) and tetramethylsilane (TMS : Si(CH_3)_4) gases on the undulated DLC film by a series of plasma Ar etching, coating process and plasma Ar etching. Static wetting angle of water was observed that double roughening structure of DLC was superhydrophobicity such as wetting angle 161°. This approach also increased in air pockets easily trap among the needle-like posts. For the low friction at nanoscale, the surface wettability of the solid lubrication played a significant role, when the DLC film modified from flat to double roughening structure, the friction was constantly inner humidity conditions. Results generally showed that humidity had insignificant effect on the nanoscale friction at superhydrophobic DLC surface. The effect of the superhydrophobic double roughening DLC and friction were discussed with the following factors: the surface morphology affinity to needle shape, a reduction of the real area of contact, graphitization and easily occur to slip at small contact interface due to self-cleaning effect.
- 2009-06-17
著者
-
Umehara Noritsugu
Department of Mechanical Science and Engineering, Nagoya University
-
JANG Young-Jun
Department of Mechanical Science and 6ngineering, Nagoya University
-
Jang Young-jun
Department Of Mechanical Science And Engineering Nagoya University
-
Kousaka Hiruyuki
Department of Mechanical Science and Engineering, Nagoya University
-
Kousaka Hiruyuki
Department Of Mechanical Science And Engineering Nagoya University
-
Umehara Noritsugu
Department Of Mechanical Science And Engineering Graduate School Of Engineering Nagoya University
関連論文
- Nanoscale Friction Behaviors of Hierarchical Superhydrophobic Structure of Diamond-like Carbon Films with Various Humidity Conditions
- Development of MAGIC Polishing Tool(Surface and edge finishing)
- MNS-15 NANOSCALE FRICTION BEHAVIORS OF HIERARCHICAL SUPERHYDROPHOBIC STRUCTURE OF DIAMOND LIKE CARBON FILMS WITH VARIOUS HUMIDITY CONDITIONS(Micro/Nanosystem Science and Technology IV,Technical Program of Oral Presentations)
- Reduction of Adhesion between Steel and Grilled Fish Protein with Ultra-Hydrophobic DLC
- MNS-01 Reduction of adhesion between steel and grilled fish protein with ultra-hydrophobic DLC(Micro/Nanosystem Science and Technology I,Technical Program of Oral Presentations)
- MNS-02 The effect of Ultraviolet ray irradiation on CNx coating's tribological property(Micro/Nanosystem Science and Technology I,Technical Program of Oral Presentations)
- Hydrodynamic Lubrication Theory Considering Electric Double Layer for Very Thin Water Film Lubrication of Ceramics
- MNS-08 Nanowear characteristics of carbon nanotube film made by surface decomposition of SiC(Micro/Nanosystem Science and Technology II,Technical Program of Oral Presentations)
- Future Developments of a Deformation - Wear Transition Map of DLC Coating
- Generation of Long and High-Density Plasma Column Using Metal-Antenna Surface Wave-Excited Plasma Source
- The Evaluation of Fracture Energy at the Interface between Grilled Fish Protein and Metal
- Effect of Plasma-On Time on the Axial Distribution of Film Thickness in Internal Diamond-Like Carbon Coating with Microwave-Excited High-Density Plasma
- Effect of Plasma-On Time on the Axial Distribution of Film Thickness in Internal Diamond-Like Carbon Coating with Microwave-Excited High-Density Plasma (Special Issue : Advanced Plasma Science and Its Applications for Nitrides and Nanomaterials)
- Wetting and Adhesion Behaviors of a-C:H Film Deposited on Nano-Scale Copper Doted Surfaces
- Microwave-Excited High-Density Plasma Column Sustained along Metal Rod at Negative Voltage