S0406-2-1 高温水環境下におけるGFRP織物材の引張クリープ特性(プラスチック基複合材料の加工と評価(2))

概要

論文の詳細を見る
Present paper deals with the creep behavior in woven GFRP underwater at elevated temperature. The tensile test of GFRP after water immersion was conducted to evaluate the residual strength after immersion at various water temperatures. The residual strength of GFRP decreased with the increase in the water temperature and the immersion time. In fact, the transition in failure mode with water immersion was ascertained from SEM observation of the fracture surface. Additionally, creep test in air and under hot water at 95℃ was conducted. The creep rupture time decreased drastically with water immersion, in contrast, creep rupture wasn't observed from the creep test in air. It was clarified that the water immersion generated the transition in the failure mode of GFRP and therefore led to the acceleration of the strength degradation.
2009-09-12