Ti-Al系合金のAl被覆
スポンサーリンク
概要
- 論文の詳細を見る
Ti_3Al is attracted attention as high specific strength and heat resistant materials in the Ti-Al intermetallic compounds. The compounds of Al-rich composition such as TiAl_3 are superior to the oxidation resistance, however, have a week point: they are very brittle at room temperature. In this study, the aluminum coating was performed on the surface of the Ti_3Al substrates by a chemical transport technique for improving the oxidation resistance. TiAl_3 layer was successfully formed on the surface of the Ti_3Al substrates by our chemical transport technique. Although the weight of the coated substrates slightly increased after the heating for 100h at 1000℃ in air, the oxidation resistance were sufficient up to 1000℃.
- サレジオ工業高等専門学校の論文
著者
関連論文
- 箔冶金法によるTi-Al系金属間化合物の組織
- Ni被覆ピッチ系炭素繊維の熱的安定性
- 電析法によるセラミック粒子分散Ni基複合材料の作製と組織
- ピッチ系炭素繊維強化Ni基複合材料の作製と機械的性質
- 6-219 中高生に対する理工系分野魅力向上の試みの一事例 : 八王子産学連携機構大学・高専学生研究成果発表会の中高生審査員の試み(口頭発表論文,(20)産学連携教育-III)
- ビスマス・テルライドの結晶構造の温度依存性
- テルル化鉛の熱膨張特性の異方性
- TiおよびVを添加したCrSi2の熱電特性
- Cu添加FeSi_2積層デバイスの作製と評価
- Cu添加FeSi_2積層デバイスの作製
- CoSi焼結体におけるNiおよびCuの添加効果
- アーク溶解法で作製したRu_2Si_3のX線結晶学的検討
- CoSi焼結体の熱電特性における不純物の効果
- アーク溶解法で作製したRu2Si3の結晶構造
- 2-223 学園都市(八王子市)における学生を主役とした地域連携の取り組み : 八王子産学公連携機構学生研究成果及び地域活性化アイデア発表会 ((18)産学連携教育-I,口頭発表論文)
- Ti-Al系合金のAl被覆
- CrSi2およびCoSi焼結体の作製方法の改善と熱電特性
- CrSi2-CoSi熱電素子の作製と熱電特性
- MnSi〜1.73焼結体の実用的製法と熱電特性
- 大気中焼結したp形FeSi2のCuおよびAl添加効果
- 大気中焼結したp 形FeSi2 のCu およびAl 添加効果
- 無添加Bi2Te3の高温におけるTeの解離・昇華
- 6-331 対戦型電気回路計算カードゲームの開発((07)教材の開発-III,口頭発表論文)
- FeSi_2 焼結体と銅板の接合条件の検討
- 7-106 10kW風力発電装置を用いた再生可能エネルギー教育とその効果((03)実験・実技-II)