4044 難燃性マグネシウム合金の疲労強度に及ぼす平均応力の影響(S19-2 マグネシウム合金の強度,S19 高機能マグネシウム合金の材料強度特性)

概要

論文の詳細を見る
Rotating bending fatigue tests and tension-compression fatigue tests were carried out to investigate effect of mean stress on fatigue strength at N=10^7 on specimens with a small artificial hole of non-combustible magnesium alloy, AMX602B(X=Ca). It was clarified that the fatigue strength at N=10^7 under tensile mean stress could be estimated using the modified Goodman diagram. However, the fatigue strength at N=10^7 under compression mean stress could not be estimated using the modified Goodman diagram. Non-propagation crack was not observed among the non-broken specimens at N=10^7 by rotating fatigue tests. The Fatigue strength at N=10^7 of the specimen with the small artificial hole is not threshold stress for crack propagation but critical stress for crack initiation. Hence it is probable that the effect of mean stress on fatigue strength at N=10^7 is small and the fatigue strength at N=10^7 under compression stress cannot be estimated using modified Goodman diagram.
社団法人日本機械学会の論文
2006-09-15