2307 工業用純チタン切欠き材の疲労強度特性について(S07-2 非鉄材料の疲労特性,S07 構造材料の疲労強度とき裂進展問題)

概要

論文の詳細を見る
Rotating bending fatigue tests on smooth and notched specimens of commercially pure titanium was curried out in order to clarify fatigue strength of notched specimen. In past study, it was found that the fatigue strength of sharp notched specimens of commercially pure titanium is not clear. So, in this study, the possibility of the prediction for the fatigue strength was considered in the viewpoint of the fatigue crack initiation life N_<i>. According to the experiment results, in the smooth and notched specimens (ρ=1.0mm), there are the clear tendency of straight line relationship between the stress amplitude and the fatigue crack initiation life. And the tendency of straight line relationship of ρ=1.0mm specimen is steeper than that of smooth specimen.
社団法人日本機械学会の論文
2007-09-07