浸炭機構に基づく真空浸炭材の炭素濃度分布予測(相変態・材料組織)

概要

論文の詳細を見る
In order to develop effective ways to estimate carbon distribution in vacuum carburized steel, the surface interaction during vacuum carburizing was investigated. 0.1mm thick specimens were vacuum carburized for sufficiently long time. The carbon content and carbide area fraction of specimens proved to be the value in equilibrium with graphite. This result shows that the graphite exists while vacuum carburizing on the surface of specimens, and that the local equilibrium between specimens and graphite is dominant factor. Carbon profile of carburized round bar was calculated on the basis of diffusion equation, on the assumption that surface carbon content is as much as the value in equilibrium with graphite. The calculatuied carbon profiles correspond to measured ones for some materials and carburizing conditions.
社団法人日本鉄鋼協会の論文
2006-04-01