Precipitation in Quenched and Aged Beryllium Containing Small Amounts of Iron
スポンサーリンク
概要
- 論文の詳細を見る
Hardness test, electrical resistivity measurement, and electron microscope observation were carried out on arc-melted beryllium specimens with up to 0.2 wt % iron which were heat-treated at 900℃ and aged at 400°to 700℃ for various times. From the results it was deduced that the amount of small dislocation loops produced probably by precipitation of excess quenched-in vacancies increased with increasing iron content, and that the vacancies combined preferentially with iron atoms, which resulted in the slowing down of their migration rate. The amount of the loops increased by the subsequent ageing, accompanied with the precipitation of iron onto the loops as well as onto other defects such as grain boundaries and dislocation lines.
- 東北大学の論文
著者
-
Koda Shigeyasu
The Research Institute For Iron Steel And Other Metals
-
Furuya Takemi
The Research Institute For Iron Steel And Other Metals
-
MOROZUMI Shotaro
The Research Institute for Iron, Steel and Other Metals
-
Morozumi Shotaro
The Research Institute For Iron Steel And Other Metals
関連論文
- Direct Observations of the Interaction between Dislocations and Precipitates in an Aluminium-Silicon Alloy
- Precipitation and Generation of Dislocations in an Al-Mg Alloy
- Precipitation in Quenched and Aged Beryllium Containing Small Amounts of Iron
- Some Mechanical Properties of Powder Extrusions of Magnesium Alloys
- Low Temperature Ultrasonic Attenuation in Germanium
- Low Temperature Ultrasonic Attenuation in Cu-Al Alloys
- Low Temperature Ultrasonic Attenuation in Magnesium and Magnesium Alloys
- Ultrasonic Attenuation in Magnesium at Low Temperatures
- Behaviour of Inclusions in Beryllium under Compression at Room Temperature
- Anomalous Change of Electrical Resistivity by Plastic Deformation in a Copper-Germanium Solid Solution Alloy
- Deformation Twinning and Stacking Fault Parameter in Cu-Ni and Cu-Mn Alloys
- The Effect of Plastic Deformation on the Cluster Formation in an Al-Cu 4% Alloy
- The Effect of θ' Phase on the Plastic Deformation of an Age-Hardenable Al-Cu 4% Alloy
- Precipitation and Generation of Dislocations in an Al-Mg Alloy
- Interaction between Dislocations and θ' Precipitates in an Aluminium-Copper Alloy
- Interface Dislocations and Glide Dislocations on θ' Precipitates in an Al-4% Cu Alloy
- Direct Observation of the Interaction of Dislocations with θ' Precipitates in an Aluminium-3.8 wt.-% Copper Alloy
- On the Interaction between Dislocations and Decomposition Products in an Al-4% Cu Alloy
- Direct Observation of the Multiplication of Dislocations in a Thin Foil of an Aluminium-Silver Alloy
- Stacking Faults of Copper-Germanium Alloys
- The Role of the Dislocation Nucleation Around Precipitates in the Mechanical Properties of a Fe-C Alloy
- Precipitation in Beryllium-Iron Alloys
- Effects of neutron irradiation on mechanical properties of iron-nitrogen alloys.