パイプ円周溶接部の内圧による溶接残留応力除去効果
スポンサーリンク
概要
- 論文の詳細を見る
The circumferential weld is one of the most popular methods of fabrication of tubular structures and pipings. Due to the weld, residual stresses (hoop and axial) on the inside of the pipe are highly tensile. The tensile residual stress is one of the factors of intergranular stress cororsion cracking of pipings. Several methods which produce compressive residual stresses along the inner surface of the welded pipe have been investigated. They are the methods using thermal elasto-plastic process; induction heating for stress improvement, backlay welding, heat sink welding, and so on. On the other hand, it may be possible to improve the residual stresses due to the circumferential weld of pipes, using some mechanical process; for example, internal pressure, explosion along the inside surface of the weldment. This paper deals with the stress release effect of internal pressure on the residual stresses due to the circumferential welds of pipes. In the first part, the analytical procedure is presented. The initial residual stress distribution is described as the sum of the "inherent stress" due to weld shrinkage and the stress induced by the "inherent stress". The incremental formula is presented for calculating the state of stresses under internal pressure. In the second part, the analytical results are compared with experimental results. The analytical results show good agreement with the experimental results. The final part of the paper deals with the assessments of stress release effect of internal pressure on the residual stresses due to the circumferential welds of pipes. The assessments are as follows. 1) The influence of welding conditions, dimensions and yield stress of pipes on the effect of internal presure. 2) Especially, the influence of heat-input; the less the heat-input of the last layer of the circumferential weld is, the more effectively the residual stresses are improved by means of internal pressure.
- 社団法人溶接学会の論文
- 1983-02-05
著者
関連論文
- 海洋工学 : 海洋構造・材料工学の動向
- 曲がりブロック溶接変形の推定法
- 224 曲面外板ブロック製造時の溶接変形推定方法の検討
- 低変態温度溶接材料を用いた角回し溶接継手の疲労強度向上
- 鋼溶接継手の疲労き裂発生寿命の一評価法
- 荷重非伝達すみ肉溶接継手の疲労強度に及ぼす降伏応力の影響
- 鋼管交差溶接継手の疲労強度 : 溶接まま継手における残留応力の影響
- 荷重非伝達すみ肉溶接継手の疲労強度に及ぼす残留応力の影響(平成3年度春季全国大会論文発表講演論文)
- 122 自動MAG溶接における施工条件と計測システム
- 海洋構造物用塗装系の耐用期間の要因解析
- 析出硬化型ステンレス鋼製フックの破断事故に関する調査
- 造船用鋼突合せ溶接継手の人工海水中疲労強度
- 人工海水中における造船用鋼板の長寿命腐食疲労強度の検討
- 造船用鋼板切欠き材の腐食疲労強度
- 低変態温度溶接材料を用いた角回溶接継手の疲労強度向上 : 溶接後熱処理による3倍化
- 227 アルミニウム合金6NO1-T5つき合わせ溶接継手の耐力
- 船体軽量化構造
- 溶接部の疲労損傷の信頼性解析
- 溶接部の疲労損傷の信頼性解析
- 溶接残留応力と疲労強度
- 海洋コンクリート構造物の設計・建造に関するシンポジウム報告
- ばら積石炭船倉内の腐食を模擬した希硫酸環境における造船用鋼の腐食および腐食疲労
- 鋼/PCハイブリッドバージの縦強度の実験的検討
- 鉱石運搬船の横強度(第2報) : コーナー部の座屈崩壊強度
- 鉱石運搬船の横強度 : 第1報 貨物倉の鉱石ペレットの挙動について
- 固有応力法の線形破壊力学への応用
- 223 ぎょう鉄(焼き曲げ)作業の定量化 : その1 : 作業分析と因子の抽出
- 角回し溶接継手の残留応力
- パイプ円周溶接部の内圧による溶接残留応力除去効果
- パイプ円周溶接により生ずる残留応力に関する一解法
- 溶接継手の疲労寿命に及ぼす荷重履歴の影響
- 510 角回し溶接継手の疲労挙動に及ぼす平均応力変動の影響
- 溶接残留応力の機械的除去に伴う材質変化の評価(昭和61年度春季全国大会論文発表講演論文)
- 229 遅れ破壊に関する一つのモデル(第2報) : 解析例
- 228 遅れ破壊に関する一つのモデル(第1報) : 水素の挙動及び脆化機構