多重熱サイクル溶接熱影響部と多重焼入材の性質について

概要

論文の詳細を見る
A atudy is made on structural features and mechanical properties, especially on notch toughness of duplicated weld heat-affected zone and multi-quenched steel similar to refined weld heat-affected zone for Si-Mn and Si-Mn-Cr-V steels by induction heating and tempering in furnace, based on the results of notch toughness surveys of welded joint for quenched and tempered steel. Refined microstructure in weld heat-affected zone is produced by rapid heating and cooling thermal cycles above Ac_1 temperature, whose maximum heating temperature are presumed to be lower in later ones. Shift of Ac_1 and Ac_3 transformation temperature was little observed, as compared with that of slower rate of heating, however, tranformation products in cooling were much influenced by heating temperature of thermal cycles, being martensitic in higher heating temperature, whereas rather ferritic in lower temperature. Hardness in duplicated weld heat-affected zone initially heated to 1350℃ was lower after subjecting to the thermal cycles of lower heating temperature. Carbide grains in those steels were rather globular than ordinarily quenched and tempered steels. Subjecting to singly quenched thermal cycle, steels had the best notch toughness, when heated to just above Ac_3 temperature followed by tempering, and toughness of singly quenched steel was improved further by repeated heating between Ac_3-Ac_1 temperature range followed by tempering. Microstructure of those steels consists of extreamly refined ferrite and globular carbides in both Si-Mn and Si-Mn-Cr-V steels, thus suggesting superior impact properties of those steels and special heat treatment for such steels. Generally steels have the poor impact properties, when repeatedly heated between Ac_3-Ac_1 temperature, however, tempering treatment gives the favourable effect on the impact properties.
社団法人溶接学会の論文
1965-07-25

多重熱サイクル溶接熱影響部と多重焼入材の性質について

スポンサーリンク

概要

著者

関連論文

スポンサーリンク