溶接ボンド部表面切欠からの脆性破壊発生に関する一考察

概要

論文の詳細を見る
The brittle fracture initiation in welded joint of 80 kg/mm^2 class high tensile steel has been studied using wide plate specimens each of which had a surface notch along the weld fusion line and weld angular distortion. Effects of the size of surface notch, the amount of weld angular distortion and weld residual stress on the brittle fracture initiation characteristics of the weld fusion line of the steel were clarified. It was found that the fracture stress data were easily explained by a newly-developed K_<1c> equation by which it was possible to express wuantitatively the effects of surface notch size and amount of angular distortion. Furthermore it was noted that the brittle fracture initiation characteristics of the welded joint with notch and angular distortion might be infered from several experiments.