オーステナイト相の析出現象に関する速度論的検討 : 2 相ステンレス鋼の溶接部における相変態現象に関する研究(第 1 報)

概要

論文の詳細を見る
Kinetics of the formation of austenite in Type 329J_1 duplex stainless steel at constant temperature was investigated as the first step to analyze the amount of the austenite in HAZ of this steel. Special attention has been paid to obtain quantitative data on the formation of austenite in the range of 950∿1150℃, because in this range, Widmanstatten austenite which occupies the greater part of the amount of austenite in HAZ after welding precipitates from ferrite grain boundary. The volume fraction of austenite was measured metallographically using an area-analyzer. As the result, it was elucidated that the formation of austenite in the range of 950∿1150℃ could be expressed by the Austin-Rickett's type equation with time exponent 'n' of 1. On the other hand, from the consideration of the activation energy for the growth of austenite, it was deduced that the formation of austenite was controlled by diffusion of nitrogen or carbon to austenite from ferrite matrix.
社団法人溶接学会の論文
1981-05-05