水中におけるサブマージアーク溶接(第 1 報) : サブマージアーク溶接法の水中溶接への適用の可能性
スポンサーリンク
概要
- 論文の詳細を見る
The feasibility of underwater welding by the submerged arc welding process is investigated. In this process, a special flux mixed water glass with MF43 is used to stabilize arc and to protect the part being welded from the sorrounding water. Welding experiments are done by using steel for welded structure SM41 of 9mm in thickness and it is ascertained that this process may be put to practical use. Main results are summerized as follows : (1) Welding arc can be generated easily and kept in stable, if only proper welding conditions are selected. Especially, good welds can be obtained easily by using a special flux mixed 40wt% water glass with MF43. (2) The weld metal includes blowholes to some extent. (3) The hardness of the underwater weld seems to be relatively low. (4) Weld metal has the tensile strength of 82% of that of base metal. (5) Cooling rate at 500℃ at bond is about 23℃/sec under water and 10℃/sec in air, the former being about only 2 times higher than the latter. The former seems to be lower value than those by any other underwater welding processes.
- 社団法人溶接学会の論文
- 1979-09-05
著者
関連論文
- 323 工具鋼と炭素鋼の摩擦圧接
- 高速溶断技術の動向
- 2017アルミニウム合金摩擦スタッド接合の強度
- Al青銅/S25C摩擦圧接継手の回転曲げ疲労強度
- 328 気孔生成現象に及ぼす雰囲気圧力の影響 : 高圧雰囲気中における重力式溶接(その3)
- 327 溶接継手の機械的性質に及ぼす雰囲気圧力の影響 : 高圧雰囲気中における重力式溶接(その2)
- 108 タングステン電極の消耗に及ぼす雰囲気圧力の影響 : 高圧下のGTA溶接における電極の消耗に関する研究(その1)
- 高圧ヘリウム雰囲気中におけるアークの特性について
- 420 高圧雰囲気中における重力式溶接(その1)
- 415 高圧雰囲気中アークの電磁制御(その1) : アーク軸方向直流磁場の溶接現象及び溶接結果に及ぼす影響