引張り予歪をうけた耐熱鋼の捩リクリープ特性について : 過歪状態における金属の挙動(第 2 報)

概要

論文の詳細を見る
The authors had reported the transition phenomenon of the increasing creep rate with the augment of prestrain, in the torsional creep test of previously twisted mild steel. In this report, we investigated the same phenomenon in the torsional creep test to HCM steel previously tensioned. From. Figs. 6∿8,We know that, on increasing the prestrain of the steel, creep rate increases abruptly, after the prestrain exceeds the ultimate-point, to about two times of creep rate before that point and appears to remain constant approximately before and after this transition zone. Fig. 9 shows the relation between strain rate γ (as to γ_1 and γ_2,see Fig. 6∿8) and the value of stress τ; on the while, Fig. 10 shows the experimental results concerning the following relation, [table] where K and n are the constants, T is the absolute temperature, Q is the activation energy and R is the gas constant. From these relations, we know that the ratio γ_2/γ_1 is constant (about 1/2) independently of the value of shear stress.
社団法人溶接学会の論文
1956-09-25